溶媒混合物によるインクジェット印刷された光放出ポリマーフィルムの厚さ均一性の調整

Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture

著者 (6件)： Xing Rubo (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...) ,  Ye Tengling (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...) ,  Ding Yan (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...) ,  Ding Zicheng (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...) ,  Ma Dongge (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...) ,  Han Yanchun (Changchun Inst. of Applied Chemistry, Chinese Acad. of Sciences State Key Lab. of Polymer Physics and Chemistry ...)
資料名： Chinese Journal of Chemistry  (Chinese Journal of Chemistry)
巻： 31  号： 11  ページ： 1449-1454  発行年： 2013年 
JST資料番号： W0337A  ISSN： 1001-604X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： この研究で,インクジェット印刷によってパターン形成されたポリ(9,9-ジ-n-オクチルフルオレン)フィルムの厚さ均一性を,溶媒混合物(より高い揮発性,より高い表面エネルギー,および低い粘着性を有する溶媒,より低い揮発性,より低い表面エネルギー,およびより高い粘性率を有する別の溶媒)の使用により向上した。インクジェット印刷されたポリ(9,9-ジ-n-オクチルフルオレン)フィルムの平均の厚さを,溶媒混合物が純粋なクロロベンゼンの代わりに使用されたときに,およそ30nmから100nmまで増加した。コーヒーリング効果によって形成された断面のような凹レンズを有するオリジナルフィルムの代わりに,よりフラットなPFO膜を形成した。この向上を,溶媒混合物における乾燥工程初めの激しいマランゴニ流と,後の乾燥工程の弱い補足的流れの併用によって説明した。形成したポリ(9,9-ジ-n-オクチルフルオレン)膜を電界発光素子の製作に用いたところ,電子特性は向上した。約80%の有効発光面積を有する画素配列が得られた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 溶媒 ,  混合物 ,  インクジェット印刷 ,  発光 ,  *高分子膜 ,  乾燥 ,  半導体素子 ,  粘度 ,  性質
準シソーラス用語： 光放出 ,  *ポリマフィルム ,  電界発光素子 ,  粘性率 ,  粘着性