ゼオライトの放電プラズマ焼結中に達成する中心温度の直接指示

Direct indication of a higher central temperature achieved during spark plasma sintering process of a zeolite

著者 (6件)： GU Shijia (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Coll. of Materials Sci. and Engineering ...) ,  ZHANG Xin (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Coll. of Materials Sci. and Engineering ...) ,  WANG Lianjun (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Coll. of Materials Sci. and Engineering ...) ,  GAN Xuehui (Coll. of Mechanical Engineering, Donghua Univ., Shanghai 201620, CHN) ,  SHEN Zhijian (Dep. of Inorganic Chemistry, Arrhenius Lab., Stockholm Univ., Stockholm SE-106 91, SWE) ,  JIANG Wan (State Key Lab. for Modification of Chemical Fibers and Polymer Materials, Coll. of Materials Sci. and Engineering ...)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 35  号： 5  ページ： 1599-1603  発行年： 2015年05月 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,焼結ままゼオライト試料の透明と不透明間の遷移を適用し,非導電性試料の放電プラズマ焼結(SPS)中の温度分布を調べた。その結果,周方向および軸方向において温度勾配が存在し,SPSにおける温度分布の直接検証を達成した。1325°Cで作製した試料は中心が透明,端が不透明であり,中心温度は端温度より高いことが示唆された。実験データのANSYSコードによる熱解析もでるでは,温度差は約25°Cであった。1315°Cで得た焼結まま試料でも軸方向の温度勾配が存在した。上部表面の透明部分は下部表面のより広く,上部表面と下部表面の温度差は約5°Cであった。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *合成ゼオライト ,  *放電焼結 ,  焼結性 ,  加熱温度 ,  *温度分布 ,  透明度 ,  プログラムパッケージ ,  応用プログラム ,  有限要素法 ,  数値解析 ,  温度勾配 ,  温度測定 ,  熱伝導率 ,  放電プラズマ焼結
準シソーラス用語： ゼオライト【合成】 ,  焼結温度 ,  ANSYS ,  熱伝導解析 ,  温度差

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (3件)： ゼオライト ,  放電プラズマ焼結 ,  中心温度