ニッケル被覆化黒鉛/二成分シリコーンゴムシーラントの電気伝導効果

The Electrical Conductive Effect of Nickel-coated Graphite/Two-component Silicone-rubber Sealant

著者 (5件)： Hu Shengfei (School of Materials Sci. and Engineering, Fac. of Light Ind., Hubei Univ. of Technol. Hubei Provincial Key Lab. of ...) ,  Li Hui (School of Materials Sci. and Engineering, Fac. of Light Ind., Hubei Univ. of Technol., Wuhan) ,  Chen Xiangxing (School of Materials Sci. and Engineering, Fac. of Light Ind., Hubei Univ. of Technol., Wuhan) ,  Zhang Chong (School of Materials Sci. and Engineering, Fac. of Light Ind., Hubei Univ. of Technol., Wuhan) ,  Liu Zuifang (School of Materials Sci. and Engineering, Fac. of Light Ind., Hubei Univ. of Technol., Wuhan)
資料名： Journal of Wuhan University of Technology. Materials Science Edition  (Journal of Wuhan University of Technology. Materials Science Edition)
巻： 28  号： 3  ページ： 429-436  発行年： 2013年 
JST資料番号： W1270A  ISSN： 1000-2413  CODEN： JWUTE8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： ニッケル被覆化黒鉛粒子と二成分シリコーンゴムを,伝導性複合材料系を形成するために混合した。複合材料の電気体積抵抗率を,応力,温度,および電流下で伝導性複合材料の導電率挙動の機構を研究するために一定の引張歪み,加熱冷却循環,電場,および繰り返し引張歪み循環の下で調べて,比較した。結果は,電気抵抗のピーク値が前に現れ,そして次に引張歪みの増加に伴い次第に増加することを示した。電気抵抗は増減する温度の間で,正の温度係数効果を示した。伝導性複合材料に5A直流を適用することは,電気抵抗の即時の増加をもたらす。しかし変化はより低い電流の下で検出されなかった。繰り返し循環歪下で,それぞれの循環の電気抵抗のピーク値は試験循環で増加した。すべての電気抵抗変化は,伝導性複合材料における崩壊および再構築された伝導ネットワークによるものと考えられた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： ニッケル ,  被覆 ,  *グラファイト ,  *シリコーンゴム ,  *シーラント ,  電気伝導 ,  二成分系 ,  *複合材料 ,  歪 ,  加熱 ,  冷却 ,  電場 ,  電気抵抗 ,  導電性
準シソーラス用語： 引張歪 ,  *黒鉛 ,  電導性