J-GLOBAL ID：201502263538003298   整理番号：15A0654076

銀のNPsを含むEr³⁺/Yb³⁺を共同ドープしたテルライトガラス中の熱処理温度に依存する1.53μmの蛍光の増強

Heat-treating temperature dependent 1.53μm fluorescence enhancement in Er³⁺/Yb³⁺ codoped tellurite glasses containing silver NPs

著者 (7件)： WU Libo (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  HUANG Bo (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  YANG Fengjing (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  QI Yawei (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  PENG Shengxi (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  ZHOU Yaxun (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN) ,  LI Jun (Coll. of Information Sci. and Engineering, Ningbo Univ., Zhejiang 315211, CHN)
資料名： Materials Letters  (Materials Letters)
巻： 152  ページ： 220-223  発行年： 2015年08月01日 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 溶融急冷とその後の熱処理の方法で製作したEr³⁺/Yb³⁺の同時ドープのテルライトガラスに銀のナノ粒子(NPs)を埋め込んで,980nmLDの励起の下でのEr³⁺の1.53μmの蛍光に及ぼす熱処理温度の影響(300,330,360,および390°C)を調査した。調査した温度範囲では熱処理温度とともに1.53μmの蛍光は増加した。これは銀のNPsの局所化された表面プラズモン共鳴(LSPR)の効果で引き起こされたEr³⁺の周りの高くなった局所電場の結果と考えられる。透過電子顕微鏡(TEM)像によると低い熱処理温度(300°C)は銀のNPsの核を作り,成長させるには十分でないが,390°Cの温度で6hの間熱処理したガラス中には平均径~13nmのほぼ球体の銀のNPsが分散していた。得られた結果は比較的高い熱処理温度が銀のNPsの生成,すなわち,Er³⁺/Yb³⁺を同時ドープしたテルライトガラス中の1.53μmの蛍光の増進に有益であることを示している。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ガラス ,  テルル化合物 ,  *エルビウム化合物 ,  *イッテルビウム化合物 ,  *ドーピング ,  *銀 ,  ナノ粒子 ,  *熱処理 ,  温度依存性 ,  *光増幅 ,  *蛍光 ,  酸化テルル ,  酸化ビスマス ,  酸化チタン ,  塩化銀
準シソーラス用語： コドーピング ,  *テルライトガラス ,  蛍光増強

分類 (2件)： ガラスの製造  (YC02020O) ,  一般及び無機化合物の蛍光・りん光(分子)  (BH06061R)

タイトルに関連する用語 (8件)： 銀 ,  Er3+ ,  共同 ,  ドープ ,  テルライトガラス ,  熱処理温度 ,  蛍光 ,  増強