超微細ラメラ構造を含む多重規模Al-Mg合金

A multi-scale Al-Mg alloy containing ultra-fine lamellar structure

著者 (4件)： LIN Yaojun (State Key Lab. of Metastable Materials Sci. and Technol., and Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  LIU Xuejian (State Key Lab. of Metastable Materials Sci. and Technol., and Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  LI Shulei (State Key Lab. of Metastable Materials Sci. and Technol., and Coll. of Materials Sci. and Engineering, Yanshan Univ. ...) ,  ZENG Zhaofen (State Key Lab. of Metastable Materials Sci. and Technol., and Coll. of Materials Sci. and Engineering, Yanshan Univ. ...)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 636  ページ： 207-215  発行年： 2015年06月11日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 公表文献ではあまり扱われていない超微細ラメラ構造を含む多重規模金属材料の研究について報告する。本研究では,高転位密度の超微細ラメラ構造から成る多重規模Al-Mg合金を,ほぼ無転位の等軸超微細,微細,及び,粗大結晶粒材と合わせて,重度冷間圧延粗大結晶粒(CG)材の部分再結晶によって製造した。多重規模Al-Mg合金は,高強度(0.2%耐力の降伏強度が焼鈍CG材の145MPaに対して約320MPa)と高延性(均一伸びが約11%)を合わせ持つ。本研究の結果,超微細ラメラ構造の体積分率は42.5%と高く,その強度も高い(0.2%耐力の降伏強度が約450MPa)ことが明らかになった。このことが,多重規模Al-Mg合金が全体として高強度であることの大きな理由である。興味深いことに,超微細ラメラ構造は同時に延性も十分に高い(均一伸びが約6%)。これは多重規模合金が高い延性を持つことに好ましい影響を与えている。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.