650°Cでのクリープ破断中の10%Crマルテンサイト系耐熱鋼溶接継手のミクロ組織とタイプIV亀裂挙動

Microstructure of 10% Cr martensitic heat-resistant steel welded joints and type IV cracking behavior during creep rupture at 650°C

著者 (6件)： ZHANG Qunbing (State Key Lab. for Mechanical Behavior of Materials, Xi’an Jiaotong Univ., Xi’an 710049, CHN) ,  ZHANG Jianxun (State Key Lab. for Mechanical Behavior of Materials, Xi’an Jiaotong Univ., Xi’an 710049, CHN) ,  ZHAO Pengfei (Dongfang Steam Turbine Ltd. Co., Deyang 618000, CHN) ,  HUANG Yong (Dongfang Steam Turbine Ltd. Co., Deyang 618000, CHN) ,  YANG Yong (State Key Lab. for Mechanical Behavior of Materials, Xi’an Jiaotong Univ., Xi’an 710049, CHN) ,  ZHAO Yale (State Key Lab. for Mechanical Behavior of Materials, Xi’an Jiaotong Univ., Xi’an 710049, CHN)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 638  ページ： 30-37  発行年： 2015年06月25日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 130~250MPa,650°Cの短時間クリープ中の新型10%Crマルテンサイト系耐熱鋼(MHRS)溶接継手のクリープ破断挙動とミクロ組織の変化を調べた。その結果,微細結晶粒化熱影響部(FGHAZ)にタイプIVの亀裂が生じた。クリープキャビティは主に前のオーステナイト結晶粒(PAG)境界の交差点に生じた。M₂₃C₆炭化物は著しく粗大化し,粗大なLaves相がPAG境界に沿うM₂₃C₆に隣接して形成し,クリープキャビティの核生成サイトとして作用した。M₂₃C₆析出物の粗大化とPAG境界のLaves相の形成と組み合わさった単位面積当たりのFGHAZの高密度のPAG交差点が,タイプIV亀裂の形成を引き起こすと考えた。Copyright 2015 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 耐熱鋼 ,  *クリープ破断 ,  マルテンサイト鋼 ,  *溶接継手 ,  炭化物 ,  Laves相 ,  *亀裂 ,  高温クリープ ,  高合金鋼 ,  オーステナイト ,  結晶粒 ,  空洞 ,  核形成 ,  析出物 ,  溶接熱影響部 ,  結晶粒微細化 ,  結晶粒界 ,  クロム含有合金
準シソーラス用語： クロム鋼 ,  旧オーステナイト

分類 (3件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： クリープ破断 ,  マルテンサイト ,  耐熱鋼 ,  溶接継手 ,  ミクロ組織 ,  タイプIV亀裂 ,  挙動