傾斜冷却板鋳造によるAl-7Si-Mg合金の微細組織変化に及ぼす鋳造パラメータの効果

Effects of Processing Parameters on Microstructure Evolution of Al-7Si-Mg Alloy by Cooling Slope Casting

著者 (6件)： THUONG Nguyen (Engineering Campus, Universiti Sains Malaysia, Structural Materials Niche Area, School of Materials and Mineral ...) ,  THUONG Nguyen (Hanoi Univ. of Sci. and Technol., School of Materials Sci. and Engineering, No. 1, Dai Co Viet street, Hanoi, VNM) ,  ZUHAILAWATI Hussain (Engineering Campus, Universiti Sains Malaysia, Structural Materials Niche Area, School of Materials and Mineral ...) ,  ABU SEMAN Anasyida (Engineering Campus, Universiti Sains Malaysia, Structural Materials Niche Area, School of Materials and Mineral ...) ,  HUY Tran Duc (Hanoi Univ. of Sci. and Technol., School of Materials Sci. and Engineering, No. 1, Dai Co Viet street, Hanoi, VNM) ,  DHINDAW Brij Kumar (Christ Univ., Mechanical Engineering Dep., Fac. of Engineering, Bangalore, IND)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 24  号： 5  ページ： 2108-2116  発行年： 2015年05月 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究は,Al-7Si-Mg合金の球状微細組織生成に及ぼす冷却板鋳造における鋳込み温度,冷却傾斜板長さ,および冷却板温度の影響を調べた。冷却傾斜板鋳造中に発達する微細組織特性を評価するために,鋳造中の傾斜板上の残留合金を急冷して,流動中の様々な段階における組織を調べた。従来の鋳造合金に現れる1次α-Alデンドライト相は,傾斜板鋳造合金では球状に変化した。より微細で均一な1次α-Al相が,低温鋳込み温度(625°C)で生成した。Al-7Si-Mg合金の微細組織に及ぼす傾斜板長さの効果は高温鋳込み(640°Cおよび660°C)では非常に大きかったが,低温鋳込み(625°C)の場合はその効果が現れなかった。合金の微細組織は,傾斜板温度増加に伴ってより粗粒化した。Copyright 2015 ASM International Translated from English into Japanese by JST.

シソーラス用語： 斜板 ,  *アルミニウム合金 ,  ケイ素含有合金 ,  マグネシウム含有合金 ,  プロセスパラメータ ,  鋳込温度 ,  α相 ,  鋳込 ,  急冷 ,  *チキソキャスト ,  傾斜角 ,  冷却器 ,  銅含有合金 ,  鉄含有合金 ,  マンガン含有合金
準シソーラス用語： *冷却スロープ鋳造 ,  *冷却傾斜式鋳造

分類 (2件)： 鋳造法,鋳込  (WC01030Q) ,  変態組織,加工組織  (WB01030N)