TC4-DTチタニウム合金の疲労クラック伝播挙動に及ぼす微細組織の効果

Effect of Microstructure on the Fatigue Crack Propagation Behavior of TC4-DT Titanium Alloy

著者 (6件)： GUO Ping (Northwestern Polytechnical Univ., State Key Lab. of Solidification Processing, School of Materials Sci. and ...) ,  GUO Ping (Northwest Inst. for Nonferrous Metal Res., 710016, Xi’an, CHN) ,  ZHAO Yongqing (Northwestern Polytechnical Univ., State Key Lab. of Solidification Processing, School of Materials Sci. and ...) ,  ZHAO Yongqing (Northwest Inst. for Nonferrous Metal Res., 710016, Xi’an, CHN) ,  ZENG Weidong (Northwestern Polytechnical Univ., State Key Lab. of Solidification Processing, School of Materials Sci. and ...) ,  LIU Jianglin (Northwestern Polytechnical Univ., State Key Lab. of Solidification Processing, School of Materials Sci. and ...)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 24  号： 5  ページ： 1865-1870  発行年： 2015年05月 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究は,様々な微細組織を持つTC4-DTチタニウム合金の疲労クラック伝播挙動を中心に検討した。熱処理を施して,α層幅およびクラスタサイズの異なる様々な微細組織を生成させた。疲労クラック伝播経路を,様々な微細組織条件で観察した。クラック先端塑性域の変形特性を分析した結果,適切な微細組織を持つ合金を得るためには2段階処理(最初にβ相域から空冷し,次に550°Cで4時間焼鈍)する事により疲労クラック伝播能を持たない優れた微細組織が得られる事が明らかになった。この結果は,クラック先端のより高い塑性変形場形成と関連していた。破壊靱性の改善には,広幅α層および粗粒αコロニーが寄与する事が明らかになった。Copyright 2015 ASM International Translated from English into Japanese by JST.

シソーラス用語： *チタン合金 ,  *疲れ亀裂成長 ,  亀裂先端 ,  クラスタ ,  β相 ,  焼なまし ,  塑性変形 ,  破壊靱性 ,  Ti-6Al-4V合金 ,  アルミニウム含有合金 ,  バナジウム含有合金
準シソーラス用語： *TC4

分類 (3件)： 機械的性質  (WB02030U) ,  金属材料  (HC05020S) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： TC4 ,  dT ,  チタニウム合金 ,  疲労クラック ,  伝播 ,  挙動 ,  微細組織