改質したコロイド状ゾル-ゲル法による高性能ZrO_2-TiO_2NF膜の作製【Powered by NICT】

Fabrication of high performance ZrO_2-TiO_2 NF membranes via a modified colloidal sol-gel process

著者 (5件)： Lu Yawei (Coll. of Chemical Engineering, State Key Lab. of Materials-oriented Chemical Engineering, National Engineering Res. ...) ,  Chen Xianfu (Coll. of Chemical Engineering, State Key Lab. of Materials-oriented Chemical Engineering, National Engineering Res. ...) ,  Wen Juanjuan (Coll. of Chemical Engineering, State Key Lab. of Materials-oriented Chemical Engineering, National Engineering Res. ...) ,  Qiu Minghui (Coll. of Chemical Engineering, State Key Lab. of Materials-oriented Chemical Engineering, National Engineering Res. ...) ,  Fan Yiqun (Coll. of Chemical Engineering, State Key Lab. of Materials-oriented Chemical Engineering, National Engineering Res. ...)
資料名： Huagong Xuebao  (Huagong Xuebao)
巻： 66  号： 9  ページ： 3769-3775  発行年： 2015年 
JST資料番号： E0215B  ISSN： 0438-1157  CODEN： HUKHAI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 平均粒径3nmの最適化したZrO_2-TiO_2複合コロイドゾルを溶媒として水を用いて修飾したコロイドゾル-ゲル法により合成することに成功した。平均細孔径5nmの管状αAl_2O_3膜を中間層として用いた。無欠陥ZrO_2-TiO_2NF膜をディップコーティング法によって中間層表面上に作製した。平均最上層厚さ200nmのZrO_2-TiO_2NF膜は約23Lm~(-2)h~(-1)(0.1 MPa)~(-1)と低いMWCO約600の比較的高い純水透過率を示した。ZrO_2-TiO_2NF膜は99.6%,低塩濃度の条件で99.2%と75.5%,pH=3と膜貫通圧力0.9MPaのCo~(2+),Sr~(2+)及びCs~+の高い保持率を示した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 純水 ,  アルミニウム ,  *ゾル-ゲル法 ,  透過率 ,  最適化 ,  *コロイド ,  *ゲル ,  pH【水素イオン指数】 ,  細孔径
準シソーラス用語： 塩濃度 ,  ディップコーティング法 ,  中間層 ,  *高性能化 , 【Automatic Indexing@JST】