新型鋳造熱間加工ダイス鋼5Cr9MoNi2SiVの焼戻脆性【Powered by NICT】

Temper brittleness of new type as-cast hot-work die steel 5Cr9MoNi2SiV

著者 (6件)： Jin Tianwen (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...) ,  Zhao Chengzhi (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...) ,  Zhang Hexin (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...) ,  Ren Quansheng (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...) ,  Fu Cehu (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...) ,  Zhang Zecheng (Key Lab. of Superlight Materials and Surface Technol. of Ministry of Education,Colledge of Material Sci. and ...)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 36  号： 8  ページ： 167-173  発行年： 2015年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 熱処理中の鋳放し鋼5Cr9MoNi2SiVの微細構造変化を,走査電子顕微鏡及び金属顕微鏡により解析した。一方種々の温度で焼戻した鋼の衝撃破壊に及ぼす粒界での元素分布をAuger電子分光法で調べた。実験結果は,鋳放し鋼5Cr9MoNi2SiVに存在する重篤な元素偏析,Cr,Mo,Mn及びVのような主な合金元素は旧オーステナイト樹枝状晶でsegreagatedであり,通常の熱処理は,偏析を改善することができるが,それを排除し,粒界の弱化をもたらすことができず,,焼戻脆化を完全に除去できないことを示した。530°Cで生じる焼戻脆化は不可逆的で,焼戻マルテンサイト脆性に属していた。鋼のembrittleness焼戻の機構は主に粒界に沿った不純物元素Pの偏析と,CrとMoは粒界でのP元素の偏析に影響する主要素である。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *クロム ,  偏析 ,  走査電子顕微鏡 ,  脆化 ,  結晶粒界 ,  鋳放し ,  *モリブデン ,  合金元素 ,  *ダイス鋼 ,  マルテンサイト ,  *鋼 ,  オーステナイト ,  *焼戻 ,  *脆性 ,  樹枝状結晶

分類 (2件)： 熱処理技術  (WC03020T) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 鋳造 ,  熱間加工 ,  ダイス鋼 ,  焼戻脆性