Mg Gd Y Nd Zr合金の高温圧縮中の動的再結晶機構【Powered by NICT】

Dynamic recrystallization mechanisms during hot compression of Mg-Gd-Y-Nd-Zr alloy

著者 (6件)： Wu Yiping (School of Materials Sci. and Engineering, Central South Univ. Key Lab. of Nonferrous Metal Materials Sci. and ...) ,  Zhang Xinming (School of Materials Sci. and Engineering, Central South Univ. Key Lab. of Nonferrous Metal Materials Sci. and ...) ,  Deng Yunlai (School of Materials Sci. and Engineering, Central South Univ. Key Lab. of Nonferrous Metal Materials Sci. and ...) ,  Tang Changping (School of Materials Sci. and Engineering, Central South Univ. Key Lab. of Nonferrous Metal Materials Sci. and ...) ,  Yang Liu (School of Materials Sci. and Engineering, Central South Univ. Key Lab. of Nonferrous Metal Materials Sci. and ...) ,  Zhong Yingying (Defense Technol. Res. and Technol. Center, China Aerospace Sci. and Ind. Corp., Beijing)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 25  号： 6  ページ： 1831-1839  発行年： 2015年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 熱間圧縮試験を450°Cで均質化したMg7Gd4Y1Nd10-0.5Zr合金と歪速度2S~(-1)について行った。動的再結晶(DRX)機構を,光学顕微鏡(OM),走査型電子顕微鏡(SEM)および透過型電子顕微鏡(TEM)により系統的に調べた。結晶学的配向情報を電子後方散乱回折(EBSD)によって得られた。結果は合金は-1.88の歪まで圧縮されるとき流動応力は,最初は谷に低下し続いて急速にピークに達し,その後再び徐々に増加することを示した。{1012}引張双晶に関連したDRXを広範囲に小さな歪で観察され,明らかな結晶粒微細化をもたらした。DRX結晶粒は第一双生児両親から約30°<0001>双晶境界の端に沿って核形成した。が大歪で,従来の連続DRX(CDRX)はしばしば元の結晶粒界に沿って小さなDRX結晶粒の形成と粒界に大きな元の結晶粒の中心から連続的に増加するミスオリエンテーションによって同定した。粒子促進核生成(PSN)の証拠も本合金で観察された。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 結晶粒界 ,  双晶 ,  *ホットプレス ,  流れ応力 ,  *合金 ,  結晶粒微細化 ,  *動的再結晶 ,  双晶境界 ,  歪速度 ,  結晶粒 ,  結晶方位 ,  核形成
準シソーラス用語： ミスオリエンテーション ,  EBSD ,  熱間圧縮 , 【Automatic Indexing@JST】

分類 (2件)： 機械的性質  (WB02030U) ,  金属工学一般  (WA01010O)

タイトルに関連する用語 (6件)： Mg ,  Gd ,  Nd ,  Zr合金 ,  高温圧縮 ,  動的再結晶