310S耐熱鋼の高温引張特性に及ぼすアルミニウムの影響【Powered by NICT】

Effect of aluminum on high temperature tensile property of 310S heat-resistant steel

著者 (5件)： Xue Panlong (State Key Lab. of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou Univ. of Technol., Gansu, Lanzhou) ,  La Peiqing (State Key Lab. of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou Univ. of Technol., Gansu, Lanzhou) ,  Liu Hui (State Key Lab. of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou Univ. of Technol., Gansu, Lanzhou) ,  Meng Qian (State Key Lab. of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou Univ. of Technol., Gansu, Lanzhou) ,  Wei Yupeng (State Key Lab. of Advanced Processing and Recycling of Non-Ferrous Metals, Lanzhou Univ. of Technol., Gansu, Lanzhou)
資料名： Gangtie Yanjiu Xuebao  (Gangtie Yanjiu Xuebao)
巻： 27  号： 7  ページ： 46-51  発行年： 2015年 
JST資料番号： W0829A  ISSN： 1001-0963  CODEN： GAYXEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： Alの0%,2%および4%の質量分率を持つ310s耐熱鋼はWS4非消費真空アーク炉を用いて調製した。これらのインゴットは950-1250°Cの温度範囲で熱間圧延した。800°Cでの機械的性質を,引張試験により測定した。破面をSEMで調べた。結果は0%と2%のAlの質量分率を持つ鋼は約210MPaの同じ強度を有することを示し,質量分率4%のAlの鋼を800°Cで最良の引張特性を有していた。ディンプルの非常に異なるサイズと深さは三鋼の引張破壊表面,鋼の破壊機構は典型的な粒界破壊であることを示しているに観測することができた。鋼におけるディンプルの体積分率はAl含有量の増加と共に増加した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 熱間圧延 ,  *鋼 ,  真空アーク ,  粒界破壊 ,  インゴット ,  体積率 ,  引張試験 ,  *耐熱鋼 ,  破面
準シソーラス用語： 破壊機構 ,  引張破壊 ,  ディンプル ,  温度範囲 ,  質量分率 ,  *引張特性 , 【Automatic Indexing@JST】