レーザ増材製造しAF1410超高強度鋼の組織と機械的性質を研究した【JST・京大機械翻訳】

Microstructure and Mechanical Properties of AF1410 Ultra-High Strength Steel Using Laser Additive Manufacture Technique

著者 (3件)： Wang Zhihui (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beihang University; Engineering Research Center of Ministry of Education on Laser Direct Manufacturing for Large Metallic Components) ,  Wang Huaming (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beihang University; Engineering Research Center of Ministry of Education on Laser Direct Manufacturing for Large Metallic Components) ,  Liu Dong (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beihang University; Engineering Research Center of Ministry of Education on Laser Direct Manufacturing for Large Metallic Components)
資料名： Zhongguo Jiguang  (Zhongguo Jiguang)
巻： 43  号： 4  ページ： 0403001-1-0403001-7  発行年： 2016年 
JST資料番号： C5022A  ISSN： 0258-7025  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 増材レーザ製造技術を用いてAF1410超高強度鋼厚板試料を調製した,均質化熱処理とAF1410鋼の従来の熱処理プロセスを組み合わせた熱処理制度をとる。その堆積状態と熱処理後のミクロ組織、硬度及び室温での引張性質の変化を解析した。結果:レーザ増材製造の堆積状態AF1410超高強度サンプル組織指向性凝固の特徴を示し,硬度はおよそ360HVであった;熱処理後,試料中のセル状凝固組織消失,組織を微細化し,微細な焼戻しマルテンサイト組織を得たが,硬度は510HVに達した。前後,室温降伏強度と引張強度はそれぞれ,1490MPAと1610MPAに達する。伸びと断面収縮率はそれぞれ12.8%と70%であった。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 厚板 ,  マルテンサイト ,  *硬度 ,  凝固組織 ,  均質化 ,  降伏強さ ,  引張 ,  熱処理 ,  引張強さ ,  生産技術 ,  焼戻 ,  伸び
準シソーラス用語： 方向性凝固 ,  *超高強度 ,  *超高強度鋼 , 【Automatic Indexing@JST】

著者キーワード (5件)： optical fabrication ,  laser additive manufacturing ,  AF1410 ultra-high strength steel ,  microstructure ,  mechanical properties

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： レーザ ,  超高強度鋼 ,  組織 ,  機械的性質 ,  研究