拡張可能なメソカーボンマイクロビーズによる超高気孔率ムライトウィスカ構造の調製と特性

Fabrication and Property of Mullite Whiskers Frameworks with an Ultrahigh Porosity by Expandable Mesocarbon Microbeads

著者 (5件)： Zeng De-Jun (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an, 710049, China) ,  Zhang Ya-Ming (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an, 710049, China) ,  Yang Jian-Feng (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an, 710049, China) ,  Wang Bo (State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an, 710049, China) ,  Matsushita Junichi (Department of Materials Science, Tokai University, Hiratsuka, 259-1292, Japan)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 99  号： 7  ページ： 2226-2228  発行年： 2016年07月 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： AlF₃,Al₂O₃,および造孔剤としてのSiO₂と追加拡張可能なメソカーボンマイクロビーズ(MCMB)の気相反応とにより,超高気孔率とのムライトウィスカ構造を調製した。ムライトウィスカーの形成時,MCMBの層状構造に起因した122%の大きな体積膨張が発生し,その結果,サンプルの膨張の発生とMCMB含有率50~90重量%で87.7%~98.2%の高気孔率につながった。気相反応によるムライトの形成により,完全ウィスカーと重ね継手構造を形成した。膨張したMCMBのウィスカ構造と焼結の空間から二峰性の細孔構造を得た。87.7~94.2%気孔率の多孔質ムライトで,剛性構造を示唆する1.7~5.4MPaの高い圧縮強度を得た。この超高気孔率での強さは,高強度ウィスカーとその強い結合を持つ構造に起因した。Copyright 2016 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ムライト ,  *多孔質体 ,  *セラミック ,  *ホイスカ ,  助剤 ,  気相反応 ,  空隙率 ,  炭素材 ,  粒状材 ,  フッ化アルミニウム ,  アルミナ ,  二酸化ケイ素 ,  細孔構造 ,  *圧縮強さ ,  重ね継手 ,  *耐熱材料 ,  メソカーボンマイクロビーズ ,  構造剛性 ,  *機械的性質 ,  *強度
準シソーラス用語： 孔形成

著者キーワード (4件)： mullite ,  porous materials ,  strength ,  whiskers

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 拡張 ,  メソカーボンマイクロビーズ ,  気孔率 ,  調製