ナノ-Al₂O₃の組込みによる高強度LPSO四元系Mg-Y-Zn-Al合金の工学的歪みの伸長

Stretching the engineering strain of high strength LPSO quaternary Mg-Y-Zn-Al alloy via integration of nano-Al2O3

著者 (6件)： Tan XingHe (Singapore Technologies Kinetics Ltd (ST Kinetics), Singapore, Singapore) ,  Tan XingHe (Department of Mechanical Engineering, National University of Singapore, Singapore, Singapore) ,  Chee Winston Keat How (Singapore Technologies Kinetics Ltd (ST Kinetics), Singapore, Singapore) ,  Chan Jimmy Kwok Weng (Singapore Technologies Kinetics Ltd (ST Kinetics), Singapore, Singapore) ,  Kwok Richard Wai Onn (Singapore Technologies Kinetics Ltd (ST Kinetics), Singapore, Singapore) ,  Gupta Manoj (Department of Mechanical Engineering, National University of Singapore, Singapore, Singapore)
資料名： Journal of Materials Science  (Journal of Materials Science)
巻： 51  号： 8  ページ： 4160-4168  発行年： 2016年04月 
JST資料番号： B0722A  ISSN： 0022-2461  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,ナノ複合材料を形成するために0.5,1.0,および1.5vol%のナノ-Al₂O₃を有する長周期積層規則化(LPSO)MgY_1.06Zn_0.76Al_0.42(at.%)合金を初めて強化する試みを行った。微細構造のキャラクタリゼーションから,凝固中のナノ複合材料中で14H LPSO相の形成を阻害するナノ-Al₂O₃の能力を明らかにした。723K(450°C)で2時間の均質化によりナノ複合材料中に微細なMg-Y-Zn-Al析出物(≦1μm)が析出した。微細Mg-Y-Zn-Al析出物およびナノ-Al₂O₃粒子は,押出中の粒子を模擬した核生成によりα-Mgの動的再結晶(DRX)を促進するのに有効であるように確立され,これはナノ複合材料中の基本テクスチャを弱め,破壊歪みの改善を招いた。その結果,破断歪みはモノリシック合金の10.8%から,NC5(ナノ-Al₂O₃粒子0.5体積%で強化されたナノ複合材料)で達成されたナノ複合材料の中で最も高い強度を有するナノ複合材料において著しく増加し15%を超えた。Copyright 2016 Springer Science+Business Media New York Translated from English into Japanese by JST.

シソーラス用語： *イットリウム合金 ,  マグネシウム含有合金 ,  亜鉛含有合金 ,  アルミニウム含有合金 ,  規則相 ,  ナノ粒子 ,  アルミナ ,  *伸び ,  *ナノ複合材料 ,  微細構造 ,  析出物 ,  動的再結晶 ,  規則合金 ,  *分散強化合金 ,  アルミナ粒子 ,  ナノ析出物 ,  長周期積層規則相 ,  破断伸び ,  ODS鋼