低温保護の化合物布のmpcmsと熱的調整性能【Powered by NICT】

MPCMs and Thermo-regulating Performance of Compound Fabric of Low Temperature Protection

著者 (5件)： Chen Xu (School of Textiles,Tianjin Polytechnic Univ.,Key Lab. of Advanced Textile Composites(Ministry of Education), Tianjin) ,  Wang Rui (School of Textiles,Tianjin Polytechnic Univ.,Key Lab. of Advanced Textile Composites(Ministry of Education), Tianjin) ,  Liu Xing (School of Textiles,Tianjin Polytechnic Univ.,Key Lab. of Advanced Textile Composites(Ministry of Education), Tianjin) ,  Li Mengxuan (School of Textiles,Tianjin Polytechnic Univ.,Key Lab. of Advanced Textile Composites(Ministry of Education), Tianjin) ,  Shi Rukun (School of Textiles,Tianjin Polytechnic Univ.,Key Lab. of Advanced Textile Composites(Ministry of Education), Tianjin)
資料名： Cailiao Gongcheng  (Cailiao Gongcheng)
巻： 43  号： 11  ページ： 65-70  発行年： 2015年 
JST資料番号： C2125A  ISSN： 1001-4381  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 相変化マイクロカプセルで仕上げた織物の低温抵抗性を研究するために,低価格のマイクロカプセルを調製した。相変化マイクロカプセルは仕上げ布の平面,綾織,無地ニット織物と低温度抵抗を試験し,評価したで仕上げた。尿素の種々の組成とシェルはマイクロカプセルのその場重合と熱性能を作製したメラミン-ホルムアルデヒド(MUF)共重合体とn-オクタデカン(マイクロC18)を含むマイクロカプセルを分析した。マイクロカプセル,平織,綾織,膨張性塗装無地ニット布の表面に被覆し,仕上げ織物の性能の多重セットを試験した。結果は,相変化マイクロカプセルの表面は平滑で,丸い,および粒子サイズは約20.6μmであることを示した。n-オクタデカンのカプセル化効率は89%であり,潜熱は約200.5J/gに達した。3種類の仕上げ織物の熱抵抗性能を31%,25%および29%それぞれ増加した。平面織物の低温抵抗性が最良であると低温の抵抗時間は約6分である。しかし,空気透過性,マイクロカプセルをわずかに減少させる。縦糸と横糸の破壊強度はそれぞれ17%と11%増加した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 透気性 ,  その場重合 ,  マイクロカプセル ,  縦糸 ,  潜熱 ,  熱特性 ,  織物 ,  横糸 ,  メリヤス ,  *低温 ,  粒度 ,  相転移
準シソーラス用語： 平織 ,  綾織 , 【Automatic Indexing@JST】

分類 (9件)： 薄膜一般  (BK14010X) ,  酸化物薄膜  (BK14050P) ,  表面硬化熱処理  (WC03030E) ,  電鋳  (WC08040Y) ,  雑音一般  (ND04010J) ,  繊維改質  (YM02050Z) ,  ゴム・プラスチック材料  (HC02030I) ,  電気めっき  (WC08023B) ,  防食  (WB03040M)

物質索引 (1件)： オクタデカン

タイトルに関連する用語 (2件)： 低温保護 ,  布