文献

J-GLOBAL ID：201602268207294631   整理番号：16A0333050

パルスプラズマ爆発処理によるAISIH13鋼上の修飾層の微細構造と性質【Powered by NICT】

Microstructure and properties of modified layer on H13 steel by pulse-plasma detonation treatment

著者 (8件)： Zou Jin (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Shanghai Key Lab. of Modern Metallurgy & Materials ...) ,  Liu Chengcheng (School of Materials Sci. and Engineering,Nanchang Hangkong Univ., Jiangxi, Nanchang) ,  Lu Deping (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang) ,  Yu Jiuming (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang) ,  Zhou Zhe (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang) ,  Zhang Linwei (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang) ,  Fu Qingfeng (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang) ,  Lu Lei (Jiangxi Key Lab. of Advanced Copper and Tungsten Materials, Jiangxi, Nanchang)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 40  号： 11  ページ： 89-93  発行年： 2015年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： H13鋼の表面はパルスプラズマデトネーション法(PPDT)により処理した。微細構造,破壊および元素分布を,光学顕微鏡,走査型電子顕微鏡及びエネルギー分散スペクトル分析によって解析した,微小硬度はKnoop硬度試験機で測定した,修飾と技術パラメータを解析し議論した。結果は,一様な厚さ,小型構造,高硬度の改質層がPPDTによって得ることができることを示した。改質層は2の領域:カラム構造ゾーンと微細結晶粒領域に分割し,電極の要素は表面に注入されると,硬度は最初に増加し,その後,改質層の深さと共に減少した。処理エネルギーの増加と共に,改質層の厚さは増加し,結晶粒径は微細になると,層の硬度は高かった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 分光分析 ,  *鋼 ,  光学顕微鏡 ,  硬度 ,  微小硬さ ,  走査電子顕微鏡 ,  *爆発 ,  結晶粒径 ,  試験装置 ,  *微細構造 ,  微結晶 ,  エネルギー散逸
準シソーラス用語： Knoop硬さ ,  元素分布 ,  *パルスプラズマ , 【Automatic Indexing@JST】

分類 (4件)： 鉄鋼材料  (WE02000W) ,  めっき一般  (WC08021T) ,  金属工学一般  (WA01010O) ,  熱処理技術  (WC03020T)

タイトルに関連する用語 (6件)： パルスプラズマ ,  爆発処理 ,  AISIH13 ,  修飾 ,  微細構造 ,  性質