MG-XAL-ZN合金のミクロ組織と硬度に及ぼす均質化焼鈍の影響を研究した。【JST・京大機械翻訳】

Influence of homogenized annealing on microstructure and hardness of Mg-xAl-Zn alloy

著者 (5件)： Han Xi (Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources,Department of Chemical Engineering and Modern Material,Shangluo University) ,  Yang Jungang (Department of Materials Science and Engineering,Xi’an University of Technology) ,  Rong Huan (Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources,Department of Chemical Engineering and Modern Material,Shangluo University) ,  Zhou Chunsheng (Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources,Department of Chemical Engineering and Modern Material,Shangluo University) ,  Liu Yanfeng (Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources,Department of Chemical Engineering and Modern Material,Shangluo University)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 41  号： 6  ページ： 67-72  発行年： 2016年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： AL含有量がそれぞれ10%、11%、12%のMG-AL-ZN合金に対して均質化焼鈍処理を行い、均質化焼鈍温度と時間が合金のミクロ組織と硬度に与える影響を検討した。結果は,合金のΒ-MG_(17)AL_(12)相が,均質化焼鈍処理の後,層状に析出することを示した。同じ温度で、均質化保温時間の延長に伴い、一部の層状組織は球状、針状組織になる。410°Cと430°Cの均質化焼鈍処理の後,合金の硬度は鋳放しと比較して増加した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 保温 ,  *均質化 ,  層状組織 ,  *焼なまし ,  *合金 ,  鋳放し ,  *硬度 ,  針状 ,  焼きなまし温度

著者キーワード (4件)： Mg-xAl-Zn alloy ,  homogenized annealing ,  microstructure ,  hardness

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： ミクロ組織 ,  硬度 ,  均質化 ,  焼鈍 ,  研究