PuNi₃型PrCo₃の合成および水素吸収-脱着特性

Synthesis of PuNi₃-type PrCo₃ and its hydrogen absorption-desorption property

著者 (5件)： Iwase Kenji (Department of Materials Science and Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi 316-8511, Japan) ,  Mori Kazuhiro (Research Reactor Institute, Kyoto University, 2-1010 Asashiro-nishi, Kumatori, Sennan, Osaka 590-0494, Japan) ,  Shimizu Shinnosuke (Department of Materials Science and Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi 316-8511, Japan) ,  Tashiro Suguru (Department of Materials Science and Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi 316-8511, Japan) ,  Suzuki Tetsuya (Department of Materials Science and Engineering, Ibaraki University, 4-12-1 Nakanarusawa, Hitachi 316-8511, Japan)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 41  号： 33  ページ： 14788-14794  発行年： 2016年09月07日 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： PuNi₃型構造をもつ金属間化合物PrCo₃を合成した。Rietveld回析法によって,正確な構造パラメータを求めた結果,正確な格子定数は,a=0.5076(1)nmおよびc=2.4831(6)nmであった。413KにおけるPrCo₃の圧力-組成(P-C)-等温曲線を測定した。最大水素容量は,0.95H/Mに達した。吸収-脱着プロセスにおいて二つのプラトーが観測され,また,水素化特性は可逆であった。X線回折を用いて,水素化相の構造変化を検討した。完全水素化相(PrCo₃H_3.8)の空間群は,R32であると決定された;元合金の金属副格子(空間群R-3m)は,水素吸収プロセスの間にR32へ変化する。完全水素化相の基本セル・CaCu₅型セル・MgZn₂型セルの体積膨張は各々,元合金の25.0%・18.4%・22.7%であった。構造変化は,非等方格子拡張を伴っていた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *プラセオジム合金 ,  *コバルト合金 ,  *金属間化合物 ,  *水素吸蔵 ,  脱着 ,  *結晶構造 ,  超格子 ,  *Rietveld法
準シソーラス用語： *水素吸収 ,  *水素脱着 ,  *超格子構造 ,  Rietveld解析

著者キーワード (5件)： P-C isotherm ,  Crystal structure ,  Superlattice structure ,  X-ray diffraction ,  Rietveld refinement

分類 (1件)： その他の金属組織学  (WB01040Y)

タイトルに関連する用語 (2件)： 水素吸収 ,  脱着