塩水噴霧環境下M152鋼の電気化学的腐食破壊機構【Powered by NICT】

Electrochemical corrosion failure mechanism of M152 steel under a salt-spray environment

著者 (8件)： Yi Pan (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Xiao Kui (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Ding Kangkang (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing State Key Lab. for Marine Corrosion and ...) ,  Wang Xu (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Yan Lidan (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Mao Chengliang (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Dong Chaofang (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing) ,  Li Xiaogang (Corrosion and Protection Center, Univ. of Sci. and Technol. Beijing, Beijing)
資料名： International Journal of Minerals, Metallurgy and Materials  (International Journal of Minerals, Metallurgy and Materials)
巻： 22  号： 11  ページ： 1183-1189  発行年： 2015年 
JST資料番号： W1051A  ISSN： 1674-4799  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： M152の腐食破壊機構は1Cr12Ni3Mo2VN(M152)の腐食挙動をより良く理解するため,材料選択の最適化のための基礎を提供し,破壊の発生を防止するために中性塩水噴霧試験を用いて研究した。さらに,この機構は,質量損失法,分極曲線,電気化学インピーダンス分光法(EIS),立体顕微鏡,走査電子顕微鏡,エネルギー分散X線分光法(EDS)を用いて調べた。結果はM152鋼は高塩水噴霧環境における,腐食,特に孔食腐食を受けることを示した。実験の初期段階では,腐食生成物の色は主にオレンジであった。その後,生成物は徐々に密,褐色物質,腐食速度の減少と一致するへ進化した。これに対応して,後期試験におけるM152のEISスペクトルもまた3の時定数を示し,低周波数ではWarburgインピーダンスを示した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： インピーダンス ,  腐食生成物 ,  *腐食 ,  エネルギー分散X線分光分析 ,  塩水噴霧試験 ,  *塩水 ,  孔食 ,  腐食速度 ,  走査電子顕微鏡 ,  *噴霧
準シソーラス用語： *水噴霧 ,  電気化学インピーダンス分光法 ,  分極曲線 ,  腐食挙動 ,  *破壊機構 , 【Automatic Indexing@JST】