J-GLOBAL ID：201602278000470938   整理番号：16A1240980

ニッケルドープチタニアの化学状態解析【JST・京大機械翻訳】

Analysis of Chemical States of Ni-doped Titania

著者 (8件)： Duan Zhicao (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Jiang Guimin (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Rong Xuequan (Faculty of Materials Science and Engineering,University of Science and Technology Beijing) ,  Yan Jikang (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Du Jinghong (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Gan Guoyou (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Yang Gang (Kunming Metallurgical Research Institute) ,  Yi Jianhong (Faculty of Materials Science and Engineering,Kunming University of Science and Technology)
資料名： Rengong Jingti Xuebao  (Rengong Jingti Xuebao)
巻： 45  号： 6  ページ： 1590-1595,1601  発行年： 2016年 
JST資料番号： W0398A  ISSN： 1000-985X  CODEN： RJXUEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ニッケルドープTIO_2の化学状態を分析した。5MOL%NIドープTIO_2粉末をゾル-ゲル法によって調製した。X線回折(XRD),透過型電子顕微鏡(TEM),走査型電子顕微鏡(STEM),X線光電子分光法(XPS),FOURIER変換赤外分光法(FT-IR),FOURIER変換赤外分光法(FT-IR),および紫外可視分光光度計(UV-VIS)を用いて,サンプルの相転移と化学状態を分析した。結果は以下を示す。NIドーピングはTIO_2の相転移と結晶成長を抑制し,TIO_2の可視光吸収スペクトルを拡大した。加熱温度の上昇とともに,NIドーピングTIO_2の格子定数は増加し,一方,TI_2P_(3/2)結合エネルギーは減少した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 可視光 ,  透過型電子顕微鏡 ,  結合エネルギー ,  走査電子顕微鏡 ,  相転移 ,  ゾル-ゲル法 ,  加熱温度 ,  X線光電子分光法 ,  結晶成長 ,  X線回折 ,  格子定数 ,  赤外分光法 ,  *ドーピング ,  紫外可視分光光度計 ,  *化学的状態
準シソーラス用語： *化学状態 , 【Automatic Indexing@JST】

著者キーワード (3件)： titana ,  Ni-doping ,  chemical states

分類 (2件)： 光化学反応  (CB08020F) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (2件)： 化学状態 ,  解析