文献

J-GLOBAL ID：201602284489036469   整理番号：16A0961609

磁気的に分離したニッケル亜鉛フェライト-グラフェン複合材料の調製とその光触媒特性【JST・京大機械翻訳】

Synthesis and Photocatalytic Properties of Magnetically Separated Ni-Zn Ferrite-Graphene Nanocomposite

著者 (6件)： Wu Shuisheng (Faculty of Chemical Engineering, Kunming University of Science and Technology; Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resource Recycle) ,  Ma Bokai (Faculty of Chemical Engineering, Kunming University of Science and Technology) ,  Jia Qingming (Faculty of Chemical Engineering, Kunming University of Science and Technology) ,  Wang Yaming (Faculty of Chemical Engineering, Kunming University of Science and Technology) ,  Dai Weili (Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resource Recycle, Nanchang Hangkong University) ,  Zhang Shiying (Hunan Key Laboratory of Application Environmental photocatalysis, Changsha University)
資料名： Wuji Huaxue Xuebao  (Wuji Huaxue Xuebao)
巻： 32  号： 4  ページ： 561-566  発行年： 2016年 
JST資料番号： C2431A  ISSN： 1001-4861  CODEN： WHUXEO  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 硝酸亜鉛、ニッケル、硝酸鉄を原料とし,マイクロ波水熱法を用いて,NI_(0.5)ZN_(0.5)FE_2O_4-グラフェンナノ複合材料を迅速に調製した。この複合材料のRAMAN及びXRD、TEM/HRTEM、XPSとVSMの結果は,13NM前後のスピネルナノフェライト粒子分散グラファイトシートにアンカー,型NieXin鉄を示した。ナノ複合材料の飽和磁化強度は28.2 A・M2KG(-1)であり,残留磁気と保磁力は基本的には0であった,超常磁性を示した。H_2O_2存在条件下で可視光照射90MIN,メチレン青(MB)の分解率が97.5%に達するのに,より良い光触媒活性をは主にグラフェンの存在に起因する光生成キャリアの分離,より多く活性における中間体,有機染料汚染物質の分解のための生成を有利にする。磁性光触媒の反復利用と触媒能力の安定性を考察し,磁気回収と再使用の要求を満たすことができる。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 水熱合成 ,  *複合材料 ,  *光触媒 ,  *ニッケル ,  超常磁性 ,  ナノ複合材料 ,  触媒活性 ,  飽和磁化 ,  *磁気 ,  X線回折 ,  *グラフェン ,  光触媒活性 ,  HRTEM ,  硝酸鉄 ,  硝酸亜鉛

著者キーワード (5件)： Ni-Zn ferrite ,  graphene ,  microwave hydrothermal ,  photocatalysis ,  characterization

分類 (2件)： 磁性材料  (NA04040H) ,  酸化物結晶の磁性  (BM06050E)

タイトルに関連する用語 (6件)： 磁気 ,  ニッケル亜鉛フェライト ,  グラフェン ,  複合材料 ,  調製 ,  触媒特性