Stu dy on the Corrosion and Adhesion Behavior of Chloridizing Metallurgy Furnace

著者 (6件)： Fu Guoyan (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing) ,  Ding Jian (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing) ,  Wei Lianqi (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing) ,  Zhang Xiaomeng (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing) ,  Liu Ya (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing) ,  Ye Shufeng (Key Lab. of Multiphase Complex Systems, Inst. of Process Engineering,Chinese Acad. of Sciences, Beijing)
資料名： Huangjin Kexue Jishu  (Huangjin Kexue Jishu)
巻： 23  号： 5  ページ： 99-104  発行年： 2015年 
JST資料番号： C2696A  ISSN： 1005-2518  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 装入物である塩化物冶金プロセスにおける化学的に複雑である。装入物の複合体成分は腐食や耐火物材料,これは耐火材料の使用寿命を低下させるに付着し,次いで塩化ばい焼金回収プロセスの工業化に強い影響を与えた。4種類の一般的な耐火物の小塊は装入物とローストに投入した。接触表面の相を解析してCaCl2を含む鉱物による高温表面腐食特性が認められた。よりAl_2O_3を含む耐火煉瓦が炉の負荷に接着剤ではないことを示唆し,そのことは彼らが条件で化学的に安定である。よりSiO_2を含む耐火煉瓦を1200°CでCaと反応するであろう。酸化鉄はAl_2O_3中の固体溶解できるので装入物は高Al_2O_3含有耐火煉瓦に執拗と1250°Cで生成する低融点の材料である。あるAl_2O_3中の固体溶解でFe_2O_3の含有量は温度上昇と共に増加した。高Al_2O_3含有耐火煉瓦の鉄の濃縮は1300°Cでより明白である。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： カルシウム ,  鉄 ,  アルミニウム ,  *ジスプロシウム ,  酸化鉄 ,  耐火材料 ,  昇温 ,  耐火物 ,  装入物 ,  高温 ,  焙焼 ,  *冶金 ,  融点 ,  *接着
準シソーラス用語： 腐食挙動 , 【Automatic Indexing@JST】

分類 (1件)： 耐火物  (YC04030N)

タイトルに関連する用語 (4件)： 冶金 ,  腐食 ,  挙動 ,  Dy