ナノ補強材としての多面体オリゴマ状シルセスキオキサン(POSS)を用いたエポキシ樹脂の機械的性質の強化【Powered by NICT】

Enhancing the mechanical properties of an epoxy resin using polyhedral oligomeric silsesquioxane (POSS) as nano-reinforcement

著者 (4件)： Mishra Kunal (School of Mechanical and Aerospace Engineering, College of Engineering, Architecture and Technology, Oklahoma State University, Stillwater, OK 74078, USA) ,  Pandey Gajendra (Center of Excellence for Advanced Modeling and Mimics (COE-AMM), Composites Solutions Business, Owens Corning Science Technology LLC, Granville, OH 43023, USA) ,  Singh Raman P. (School of Mechanical and Aerospace Engineering, College of Engineering, Architecture and Technology, Oklahoma State University, Stillwater, OK 74078, USA) ,  Singh Raman P. (School of Materials Science and Engineering, College of Engineering, Architecture and Technology, Oklahoma State University, Tulsa, OK 74106, USA)
資料名： Polymer Testing  (Polymer Testing)
巻： 62  ページ： 210-218  発行年： 2017年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,多面体オリゴマ状シルセスキオキサン(POSS),ハイブリッド有機-無機ナノ充填剤で強化したエポキシの機械的および破壊特性について報告した。POSS強化エポキシ樹脂のユニークな特性は,処理問題を克服するために利用した。種々の有機置換基(メタクリル,グリシジル,トリシラノールフェニル)とPOSS分子はエポキシ樹脂に添加された0.5と8wt%の間の充填量での直接混合した。POSSの添加は平均130%と400%のエポキシ樹脂の骨折靭性及び骨折の仕事を増加させ,それぞれ有意に観察されたが,有意な変化は曲げ弾性率と曲げ強さでは観察されなかった。走査電子顕微鏡(SEM)は,POSS挿入による外因性強靭化機構の証拠を調べるために破面上に行った。エポキシ樹脂とPOSSの化学的相互作用を,Fourier変換赤外(FTIR)を用いて調べた。最後に,示差走査熱量測定(DSC)によると,POSSの包含から生じるガラス転移温度(T g)の変化を測定した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 骨折 ,  走査電子顕微鏡 ,  靱性 ,  *補強材料 ,  示差走査熱量測定 ,  *エポキシ樹脂 ,  破面 ,  ガラス転移点 ,  曲げ強さ
準シソーラス用語： 化学的相互作用 ,  強靱化 ,  曲げ弾性係数 ,  充填量 ,  破壊特性 ,  ナノフィラー , 【Automatic Indexing@JST】

分類 (2件)： 機械的性質  (YH02022L) ,  エポキシ樹脂  (YH07040I)

タイトルに関連する用語 (8件)： 補強材 ,  多面体 ,  オリゴマ ,  シルセスキオキサン ,  POSS ,  エポキシ樹脂 ,  機械的性質 ,  強化