文献

J-GLOBAL ID：201702211335691993   整理番号：17A1963942

触媒層の間隙率と厚さに及ぼすカーボンナノチューブ森林の高さと直径依存性【Powered by NICT】

Height and diameter dependence of carbon nanotube forests on the porosity and thickness of catalytic layers

著者 (6件)： Papa Z. (University of Szeged, Department of Optics and Quantum Electronics, H-6720 Szeged, Dom ter 9. Hungary) ,  Kecsenovity E. (University of Szeged, Department of Applied and Environmental Chemistry, H-6720 Szeged, Rerrich B. ter 1. Hungary) ,  Fejes D. (University of Szeged, Department of Applied and Environmental Chemistry, H-6720 Szeged, Rerrich B. ter 1. Hungary) ,  Budai J. (University of Szeged, Department of Optics and Quantum Electronics, H-6720 Szeged, Dom ter 9. Hungary) ,  Toth Z. (University of Szeged, Department of Oral Biology and Experimental Dental Research, H-6720 Szeged, Tisza Lajos krt. 64. Hungary) ,  Hernadi K. (University of Szeged, Department of Applied and Environmental Chemistry, H-6720 Szeged, Rerrich B. ter 1. Hungary)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 428  ページ： 885-894  発行年： 2018年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： CNTの品質およびFe-Co触媒の特性の面から研究した高度に秩序化したカーボンナノチューブ(CNT)フォレストの合成。CNTフォレストは触媒化学気相蒸着により成長させた。触媒の量を二つの方法で変化させた(1)異なったナノ構造を持つ触媒層を溶着チャンバー内の種々のアルゴン圧力を適用することにより,パルスレーザ蒸着で作製した,(2)コンパクトな触媒層は,1~5nm範囲の種々の厚さの堆積した。著者らの結果は,触媒層のナノ構造と層の厚さの両方が触媒粒子の形成に重要な役割を持っており,従ってCNT成長の特性に及ぼすことを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノ構造 ,  *触媒 ,  品質 ,  アルゴン ,  *カーボンナノチューブ ,  *空隙率 ,  パルスレーザ蒸着 ,  蒸着
準シソーラス用語： チャンバ ,  溶着 ,  触媒化学 ,  *直径依存性 ,  *触媒層 , 【Automatic Indexing@JST】

著者キーワード (3件)： カーボンナノチューブフォレスト ,  CVD合成 ,  触媒層の構造

分類 (1件)： その他の無機化合物の薄膜  (BK14060A)

タイトルに関連する用語 (6件)： 触媒層 ,  間隙率 ,  厚さ ,  カーボンナノチューブ ,  森林 ,  直径依存性