引張及び再結晶後のチタンのミクロ組織の発達【Powered by NICT】

Microstructure evolution of titanium after tensile and recrystallisation

著者 (4件)： Wronski S. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059 Krakow, Poland) ,  Jedrychowski M. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059 Krakow, Poland) ,  Tarasiuk J. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059 Krakow, Poland) ,  Bacroix B. (LSPM, CNRS, Universite Paris XIII, 99, av. J.B. Clement, 93 430 Villetaneuse, France)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 692  ページ： 113-126  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 引張変形中のチタンTi40の定性的及び定量的挙動は,その後の再結晶過程に及ぼす変形と双晶の影響と共に調べた。この目的のために,調査した材料は,相互に垂直な方向での伸長を行った。引張試験は8%と16%の変形まで行った。続いて,材料を,電子後方散乱回折法を用いて調べた。微細構造と方位差プロファイルの解析は,横方向に引き伸ばされた材料は多数の双晶構造の生成によって特徴づけられることを示した。双晶{1012}< 1011>の多数が観察されたが,圧延方向{11 22}<-1 123>における延伸試料における双晶構造は,めったに観察されなかった。変形中に得られた双晶構造は,再結晶化過程に影響を及ぼす,主に再結晶動力学。この現象は再結晶時間の関数としての粒方位の広がり及び結晶粒径のようなパラメータの分析により確認した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒径 ,  引張変形 ,  微細構造 ,  *引張 ,  双晶 ,  *再結晶 ,  引張試験 ,  延伸 ,  *チタン
準シソーラス用語： 圧延方向 ,  EBSD , 【Automatic Indexing@JST】

著者キーワード (5件)： チタン ,  EBSD ,  引張試験 ,  双晶化 ,  再結晶

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 引張 ,  再結晶 ,  チタン ,  ミクロ組織 ,  発達