高温CO_2におけるNi合金の酸化挙動への機構的洞察【Powered by NICT】

Mechanistic insights into the oxidation behavior of Ni alloys in high-temperature CO₂

著者 (8件)： Oleksak Richard P. (National Energy Technology Laboratory, 1450 Queen Ave SW, Albany, OR, 97321, USA) ,  Baltrus John P. (National Energy Technology Laboratory, 626 Cochrans Mill Rd, Pittsburgh, PA, 15236, USA) ,  Nakano Jinichiro (National Energy Technology Laboratory, 1450 Queen Ave SW, Albany, OR, 97321, USA) ,  Nakano Jinichiro (AECOM, P.O. Box 1959, Albany, OR 97321, USA) ,  Nakano Anna (National Energy Technology Laboratory, 1450 Queen Ave SW, Albany, OR, 97321, USA) ,  Nakano Anna (AECOM, P.O. Box 1959, Albany, OR 97321, USA) ,  Holcomb Gordon R. (National Energy Technology Laboratory, 1450 Queen Ave SW, Albany, OR, 97321, USA) ,  Dogan OEmer N. (National Energy Technology Laboratory, 1450 Queen Ave SW, Albany, OR, 97321, USA)
資料名： Corrosion Science  (Corrosion Science)
巻： 125  ページ： 77-86  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高純度CO_2における短時間とArを含む≦1ppb O_2で同様に酸化したNi超合金の結果を提示した。酸化表面の詳細な分析は,二曝露環境のための顕著な類似性を明らかにし,O_2不純物は高温CO_2における酸化過程を制御する示唆された。選択的酸化は外方拡散によって成長させたCrリッチ酸化物層をもたらし,一方,金属に残されたCr空孔は酸化物/金属界面で大きなボイドの形成に寄与している。とは異なり合金表面の大部分で,第二相金属炭化物の酸化挙動は二種類の環境でかなり異なっていた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： クロム ,  超合金 ,  第二相 ,  *酸化 ,  *高温 ,  炭化物 ,  アルゴン ,  界面 ,  *ニッケル合金 ,  *ニッケル ,  *合金 ,  不純物
準シソーラス用語： 酸化物層 ,  選択酸化 ,  *酸化挙動 , 【Automatic Indexing@JST】