結晶塑性理論に基づく歪速度の広範囲の下での42CrMo鋼の構成モデル【Powered by NICT】

Constitutive model of 42CrMo steel under a wide range of strain rates based on crystal plasticity theory

著者 (4件)： Lu Yesen (State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu, Sichuan 610031, China) ,  Zhu Zhiwu (State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu, Sichuan 610031, China) ,  Li Dingyuan (School of Mechanics and Engineering, Southwest Jiaotong University, Chengdu Sichuan 610031, China) ,  Xie Qijun (School of Mechanics and Engineering, Southwest Jiaotong University, Chengdu Sichuan 610031, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 679  ページ： 215-222  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 機械的性質と42CrMo鋼の応力-歪関係を研究するために,準静的圧縮と引張試験と動的圧縮試験に供した。結果は,準静的および動的荷重の下で明白である歪速度効果を示した。断熱温度上昇に起因する歪硬化と熱軟化の間の競合である。材料の挙動は引張および圧縮荷重下で対称である。熱活性化理論を用いて,変形機構を説明した。異なる活性化条件と高歪速度感受性Peierls応力は,準静的および動的負荷への応答で観察された異なる機械的特性の主な原因である。結晶塑性理論に基づく修正モデルを提案した。巨視的歪速度はせん断速度の変化であると考えられ,温度上昇は硬化則を考慮した。モデルは42CrMo鋼の準静的および動的機械的挙動を非常によく記述することを確認し,特に歪硬化と熱軟化の影響した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *歪速度 ,  昇温 ,  引張 ,  圧縮荷重 ,  引張試験 ,  *構成モデル ,  剪断速度 ,  歪硬化
準シソーラス用語： 高ひずみ速度 ,  歪速度感受性 ,  変形機構 ,  熱活性化 ,  応力-歪関係 ,  *42CrMo鋼 ,  *結晶塑性 , 【Automatic Indexing@JST】