細粒ルチル精鉱の流動層造粒に関する研究【Powered by NICT】

Study on the fluidized bed granulation of fine-grained rutile concentrate

著者 (6件)： Chen Xuling (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China) ,  Zhou Xunwei (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China) ,  Gan Min (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China) ,  Fan Xiaohui (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China) ,  Ji Zhiyun (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China) ,  Tian Zhiyuan (School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China)
資料名： Powder Technology  (Powder Technology)
巻： 315  ページ： 53-59  発行年： 2017年 
JST資料番号： B0730A  ISSN： 0032-5910  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 中国におけるルチル精鉱の粒径は塩素化プロセスの要求を満たすためにあまりに微細すぎるのである。塩素処理前の約100μm直径を有するミセルへと粒状化する必要がある。流動層造粒法はミセルを調製するために使用し,造粒に及ぼす影響因子を調べた。結果は,相対的に高い濃度と噴霧時間の増加は粒子の成長に有利であることを示した。良好な造粒性能を得るために,バインダー溶液,充填率と噴霧時間の適切な濃度はそれぞれ0.8%,1.8%及び60分であった粘結剤としてカルボキシメチルセルロースナトリウム(CMC)を用いた。最終生成物の平均直径は均一な粒子サイズ分布を持つ約103μmであり,粒子の球形度は改善された。ミセルの造粒機構は凝集と層成長は,造粒プロセス中に共存することを示した。粒子成長は,造粒の初期段階での凝集成長によって制御されると,皮膜は造粒の端部での主成長方法である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微粒子 ,  噴霧 ,  *造粒 ,  塩素処理 ,  *ルチル ,  粘結剤 ,  中華人民共和国 ,  凝集 ,  ミセル ,  *精鉱 ,  粒径 ,  皮膜 ,  *流動層 ,  粒度分布 ,  塩素化

著者キーワード (5件)： ルチル濃縮物 ,  微粒子 ,  流動造粒 ,  凝集 ,  層形成

分類 (1件)： 固体の製造・処理一般  (XD03021O)

タイトルに関連する用語 (5件)： 細粒 ,  ルチル ,  精鉱 ,  流動層造粒 ,  研究