高温におけるアルミニウム再融解からの脱脂高温ドロスを用いた水素の溶融塩高生産【Powered by NICT】

Molten salt-enhanced production of hydrogen by using skimmed hot dross from aluminum remelting at high temperature

著者 (7件)： Li Peng (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Wang Jun (College of Chemical Engineering, China University of Petroleum, Qingdao 266580, PR China) ,  Zhang Xiuxia (College of Chemical Engineering, China University of Petroleum, Qingdao 266580, PR China) ,  Hou Xinmei (State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Yan Bingji (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Guo Hongwei (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Seetharaman Seshadri (Department of Materials Science and Engineering, Royal Institute of Technology, SE-10044 Stockholm, Sweden)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 42  号： 18  ページ： 12956-12966  発行年： 2017年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アルミニウムの二次製造で発生する脱脂高温ドロスは高量の金属アルミニウムを含み,また潜在的熱。アルミニウム再融解産業からの脱脂高温ドロスを用いた水素発生のための革新的方法をこの研究で提案した。高温で水素発生変化の観点から脱脂ドロスと水蒸気間の反応挙動を研究した。その結果,ドロス中の固有の塩は水蒸気雰囲気中で非晶質とγAl_2O_3生成物層を溶解することにより600 850°Cの温度領域での水素発生を加速できることを示した。最大アルミニウム転化率は60%以上であることが分かり,30wt%Alを含む脱脂ドロスは非等温試験で用いた場合,水素発生速度は60cm~3g~( 1)分~ 1以上であった。種々の量の塩添加物と温度のアルミナ層の組織応答に関連した機構を検討した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 添加剤 ,  *脱脂 ,  非晶質 ,  *高温 ,  アルミナ ,  *水素 ,  *アルミニウム ,  *融解塩 ,  転化率
準シソーラス用語： 温度範囲 ,  水素発生 ,  *再融解 , 【Automatic Indexing@JST】

著者キーワード (5件)： 脱脂ドロス ,  アルミニウム再融解 ,  水素生産 ,  塩流束 ,  加速

分類 (1件)： 気体燃料の製造  (YE02030F)

タイトルに関連する用語 (6件)： アルミニウム ,  再融解 ,  脱脂 ,  ドロス ,  水素 ,  溶融塩