異なる回転速度での連続駆動摩擦溶接したグレード2シームレスチタン管の微細構造と機械的特性【Powered by NICT】

Microstructure and mechanical characterization of continuous drive friction welded grade 2 seamless titanium tubes at different rotational speeds

著者 (4件)： Palanivel R. (Department of Mechanical Engineering Science, University of Johannesburg, Auckland Park Kingsway Campus, Johannesburg 2006, South Africa) ,  Laubscher R.F. (Department of Mechanical Engineering Science, University of Johannesburg, Auckland Park Kingsway Campus, Johannesburg 2006, South Africa) ,  Dinaharan I. (Department of Mechanical Engineering Science, University of Johannesburg, Auckland Park Kingsway Campus, Johannesburg 2006, South Africa) ,  Hattingh D.G. (Department of Mechanical Engineering, Nelson Mandela Metropolitan University, Port Elizabeth 6001, South Africa)
資料名： International Journal of Pressure Vessels and Piping  (International Journal of Pressure Vessels and Piping)
巻： 154  ページ： 17-28  発行年： 2017年 
JST資料番号： H0395A  ISSN： 0308-0161  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 摩擦溶接は薄い金属管を接合するためにほぼ理想的なプロセスである。外径60mm,壁厚3.9mmのグレード2チタン管を,摩擦圧接法により接合した。微細構造に及ぼす回転速度の影響を五種の異なる速度で評価した。プロセスパラメータは溶接中に記録した。微細構造を光学顕微鏡と電子後方散乱図を用いて観察した。結果は回転速度は,プロセスパラメータ,ミクロ組織と継手の健全性に有意な影響を及ぼしたことを明らかにした。回転速度の増加は,摩擦パワー入力のトルクと速度を減少させ,溶接継続時間を延長した。変形速度は回転速度と共に増加し,溶接部の結晶粒を微細化した。粒径はフラッシュに対する溶接部の中心から粗大化することが観察された。熱影響部(HAZ)における結晶粒構造は母材と同じであった。2200rpmの回転速度で達成された98.3%の最大継手効率。微小硬さ,破壊位置と破壊表面の詳細を報告した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微小硬さ ,  破面 ,  プロセスパラメータ ,  *回転数 ,  粒径 ,  健全性 ,  金属管 ,  溶接部 ,  *溶接 ,  *摩擦溶接 ,  トルク ,  結晶粒 ,  光学顕微鏡 ,  *微細構造
準シソーラス用語： 継手効率 , 【Automatic Indexing@JST】

著者キーワード (5件)： チタン ,  管 ,  摩擦溶接 ,  Microstructure ,  引張強さ