窒化浸炭した低温作業工具鋼とその形成機構の鉱脈状粒界構造のTEMによる研究【Powered by NICT】

TEM study on the vein-like grain boundary structures in nitrocarburized cool-work tool steels and its formation mechanism

著者 (5件)： Chen Wanglin (School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou City, Guangdong Province 510006, PR China) ,  Chen Wanglin (School of Materials Science and Engineering, Anhui University of Technology, Maanshan City, Anhui Province 243002, PR China) ,  Zhang Daoda (Jiangxi Mechanical Scientific Institute, Nanchang City, Jiangxi Province 330000, PR China) ,  Yao Dengcan (Jiangxi Mechanical Scientific Institute, Nanchang City, Jiangxi Province 330000, PR China) ,  Meng Xianna (School of Metallugrical Engineering, Anhui University of Technology, Maanshan City, Anhui Province 243002, PR China.)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 324  ページ： 376-381  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 脈状粒界(VLGB)構造は,一般的に窒化および窒化浸炭した鉄系材料に現れた。このようなVLGB構造はその機械的性質のために非常に悪い。VLGB構造の形成機構は不明である。ここでは,透過型電子顕微鏡および電子プローブX線微量分析は,詳細なミクロ組織と540°Cと580°Cで窒化浸炭したCr12MoV冷間加工工具鋼におけるVLGB構造の形成機構を明らかにするために用いた。VLGB構造は完全に斜方晶(Cr,Fe)7C_3相から構成されている,高密度ミクロ双晶と積層欠陥であり,(Cr,Fe)7C_3型VLGB構造とマトリックス間の特異的結晶学関係は(101)α∥(2 4 1 )C+7.5°と[1 11]α∥[1 02]。(Cr,Fe)7C_3型VLGB構造の形成は,C/Cr濃度,弾性歪エネルギー,低エネルギー界面と生成エンタルピーVLGB構造と密接に関連している。同様の解釈は,他の窒化浸炭または窒化合金鋼のVLGB構造の形成を解明するために行った。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *工具鋼 ,  界面 ,  斜方晶系 ,  *窒化 ,  積層欠陥 ,  機械的性質 ,  *浸炭窒化 ,  微量分析 ,  双晶 ,  透過型電子顕微鏡 ,  *低温 ,  冷間加工 ,  *結晶粒界 ,  合金鋼
準シソーラス用語： *形成機構 , 【Automatic Indexing@JST】

著者キーワード (5件)： Cr12MoV低温作業工具鋼 ,  Nitrocarburizing ,  静脈様粒界構造 ,  (CrFe)は_7C_3 ,  相変態