TA15合金における2相領域熱処理中のラメラα相の発達【Powered by NICT】

Evolution of lamellar α phase during two-phase field heat treatment in TA15 alloy

著者 (4件)： Sun Zhichao (State Key Lab of Solidification Processing, Department of Materials Science and Engineering, Northwestern Polytechnical University, P. O. Box 542, Xi’an, Shaanxi, 710072, China) ,  Wu Huili (State Key Lab of Solidification Processing, Department of Materials Science and Engineering, Northwestern Polytechnical University, P. O. Box 542, Xi’an, Shaanxi, 710072, China) ,  Sun Junzhi (State Key Lab of Solidification Processing, Department of Materials Science and Engineering, Northwestern Polytechnical University, P. O. Box 542, Xi’an, Shaanxi, 710072, China) ,  Cao Jing (State Key Lab of Solidification Processing, Department of Materials Science and Engineering, Northwestern Polytechnical University, P. O. Box 542, Xi’an, Shaanxi, 710072, China)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 42  号： 32  ページ： 20849-20856  発行年： 2017年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 全熱処理過程でTA15合金における一次層状α相の進化を調べるために実施した相場熱処理実験。一方各種断熱履歴を持つ空気冷却中の一次と二次ラメラαの変化の両方を調べた。結果は加熱中の一次ラメラα相の変態機構は低いα/β領域における薄いラメラの変態と高いα/β領域で分岐ラメラの分解から生じる小さなラメラの溶解であることを示した。保持過程で,一次ラメラαの体積分率は減少し,平均厚さは増加し,平均長さの変化傾向は複雑である。ニ相場熱処理後の冷却モードは絶縁歴史と結合させたとき,体積分率の変動傾向は,非単調な方法を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *熱処理 ,  *α相 ,  *合金 ,  空気冷却 ,  体積率
準シソーラス用語： *TA15 , 【Automatic Indexing@JST】

著者キーワード (5件)： TA15合金 ,  原発性ラメラα ,  二次ラメラα ,  微細構造進化 ,  相場熱処理

分類 (2件)： その他の金属組織学  (WB01040Y) ,  気体燃料の輸送,供給,貯蔵  (YE02060M)

タイトルに関連する用語 (6件)： TA15 ,  合金 ,  熱処理 ,  ラメラ ,  α相 ,  発達