中性子照射下での酸化物分散強化合金のナノクラスタの安定性【Powered by NICT】

Stability of nanoclusters in an oxide dispersion strengthened alloy under neutron irradiation

著者 (7件)： Liu Xiang (Department of Nuclear, Plasma, and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, USA) ,  Miao Yinbin (Nuclear Engineering Division, Argonne National Laboratory, Lemont, IL 60439, USA) ,  Wu Yaqiao (Department of Materials Science and Engineering, Boise State University, Boise, ID 83725, USA) ,  Wu Yaqiao (Center for Advanced Energy Studies, Idaho Falls, ID 83401, USA) ,  Maloy Stuart A. (Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM 87545, USA) ,  Stubbins James F. (Department of Nuclear, Plasma, and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, USA) ,  Stubbins James F. (International Institute for Carbon Neutral Energy Research (WPI-I2CNER), Kyushu University, 744 Motooka, Nishi-ku, Fukuoka 819-0395, Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 138  ページ： 57-61  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ここでは,中性子照射した酸化物分散強化合金におけるナノクラスタの原子プローブトモグラフィーの結果を報告した。ターゲット温度300°Cと450°Cで5dpaまで照射に続いて,より少ない大きなナノクラスタが見出され,残留ナノクラスタは1.8nmの平衡Guinier半径に到達する傾向がある。放射線量の増加に伴って,ナノクラスタにおけるピーク酸素とチタン(イットリウムではなく)濃度の明らかな減少が観察され,これは原子量,溶解度,拡散性,及び化学結合議論により説明した。化学修飾は平衡サイズは二つの競合するプロセス:放射線促進拡散と衝突溶解のバランスを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 放射線 ,  *分散強化 ,  原子量 ,  *中性子照射 ,  放射線量 ,  *合金 ,  溶解度 ,  溶解 ,  チタン ,  化学結合 ,  *ナノクラスタ ,  *酸化物 ,  イットリウム
準シソーラス用語： 原子プローブトモグラフィー ,  *ODS鋼 , 【Automatic Indexing@JST】

著者キーワード (4件)： 酸化物分散強化(ODS)合金 ,  Microstructure ,  原子プローブトモグラフィー ,  中性子照射

分類 (1件)： 分散強化合金  (WE04030R)

タイトルに関連する用語 (4件)： 中性子照射 ,  酸化物分散強化合金 ,  ナノクラスタ ,  安定性