添加と焼結-HIPによるち密化炭素ボートによる超微細WC-10Co複合粉末の合成【Powered by NICT】

Synthesis of ultrafine WC-10Co composite powders with carbon boat added and densification by sinter-HIP

著者 (6件)： Yang Qiumin (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Yang Jiangao (Advanced Corporation for Materials & Equipments, Changsha 410118, China) ,  Yang Jiangao (Engineering Research Center of High-efficiency Development and Application Technology of Tungsten Resources, Ministry of Education, Ganzhou 341000, China) ,  Yang Hailin (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Ni Guohua (Advanced Corporation for Materials & Equipments, Changsha 410118, China) ,  Ruan Jianming (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
資料名： International Journal of Refractory Metals & Hard Materials  (International Journal of Refractory Metals & Hard Materials)
巻： 62  号： PB  ページ： 104-109  発行年： 2017年 
JST資料番号： H0059B  ISSN： 0263-4368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 炭素欠損相と遊離炭素を含まないWC-10Co複合材料粉末を還元-炭化プロセスにおける添加炭素ボート法により合成することができた。炉における炭素ボートは還元-炭化プロセス,炭素拡散速度は炭化速度と一致した中に自然炭素活量のバランスをとることができた。複合材料粉体の平均粒径は175nmであった部分的にファセット化した,わずかに長く伸びた形であった。この方法により,従来手法に比べてより低い反応温度とより短い保持時間の明確な利点を有している。さらに,焼結-HIP炉における超微細WC-10Co複合粉体の圧密を調べた。圧密後,添加した炭素ボートで合成した粉末からのWC-10Co合金は均一な微細粒ミクロ組織と良好な組合せた機械的性質硬さ1985±50HVと破壊靭性10.2MPa m~1/2二相合金を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 拡散速度 ,  *緻密化 ,  二相合金 ,  反応温度 ,  活量 ,  *炭素 ,  保持時間 ,  硬度 ,  *ボート ,  圧密 ,  炭化 ,  破壊靱性 ,  ファセット
準シソーラス用語： *複合粉 , 【Automatic Indexing@JST】

著者キーワード (4件)： 超微細WC-Co粉末 ,  カーボンボート ,  複合炭素含有量 ,  超微細粒超硬合金

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  圧粉,焼結  (WC02030X)

タイトルに関連する用語 (8件)： 焼結 ,  HIP ,  ち密化 ,  炭素 ,  ボート ,  超微細 ,  WC ,  複合粉末