多結晶銅の異周速圧延による集合組織の効果【Powered by NICT】

Texture effects due to asymmetric rolling of polycrystalline copper

著者 (5件)： Uniwersal A. (AGH University of Science and Technology, Faculty of Metals Engineering and Industrial Computer Science, al. Mickiewicza 30, 30-059, Krakow, Poland) ,  Wronski M. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059, Krakow, Poland) ,  Wrobel M. (AGH University of Science and Technology, Faculty of Metals Engineering and Industrial Computer Science, al. Mickiewicza 30, 30-059, Krakow, Poland) ,  Wierzbanowski K. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059, Krakow, Poland) ,  Baczmanski A. (AGH University of Science and Technology, Faculty of Physics and Applied Computer Science, al. Mickiewicza 30, 30-059, Krakow, Poland)
資料名： Acta Materialia  (Acta Materialia)
巻： 139  ページ： 30-38  発行年： 2017年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 異周速圧延による,多結晶銅の集合組織変化を実験的に調べ,理論的に解析した。骨格線に沿った配向分布関数とその強度を検討した。非対称圧延後の集合組織成分は,横方向の周りで約,対称圧延後のそれらと比較して回転していることが分かった。回転角は圧延非対称性比の関数として特徴的な集合組織成分を決定した。圧延シート厚さ方向集合組織不均一性も調べた。圧延集合組織の理論的予測は二つの結晶変形モデルを用いて行った。方位分布関数,集合組織成分の回転と試料の厚さを横切ってそれらの変化を決定し,理論結果と比較した。非対称圧延集合組織後の最終方位の安定性を試験した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *異周速圧延 ,  結晶 ,  対称性 ,  不均一性 ,  *集合組織 ,  *圧延 ,  *多結晶 ,  圧延組織 ,  方位分布関数 ,  回転角 ,  *銅 ,  予測 ,  分布関数 ,  非対称性

著者キーワード (5件)： 非対称圧延 ,  多結晶銅 ,  テクスチャ不均一性 ,  結晶変形モデル ,  配向安定性

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： 多結晶 ,  銅 ,  異周速圧延 ,  集合組織