還元熱処理ステップを持つSr_4(Sr_2Ta_2)O_11複合ペロブスカイトの固相合成と分析【Powered by NICT】

Solid state synthesis and analyses of Sr₄(Sr₂Ta₂)O₁₁ complex perovskite with reduced heat treatment steps

著者 (7件)： Bradha M. (PSG Institute of Advanced Studies, Coimbatore, 641 004, T.N., India) ,  Kavitha K. (PSG Institute of Advanced Studies, Coimbatore, 641 004, T.N., India) ,  Vijayaraghavan T. (PSG Institute of Advanced Studies, Coimbatore, 641 004, T.N., India) ,  Vijila G. (Dept. of Biomedical Engineering, PSG College of Technology, Coimbatore, 641 004, T.N., India) ,  Suresh P. (Dept. of Biomedical Engineering, PSG College of Technology, Coimbatore, 641 004, T.N., India) ,  Udhayabanu V. (Dept. of Metallurgical Engineering, PSG College of Technology, Coimbatore, 641 004, T.N., India) ,  Ashok Anuradha (PSG Institute of Advanced Studies, Coimbatore, 641 004, T.N., India)
資料名： Materials Characterization  (Materials Characterization)
巻： 128  ページ： 142-147  発行年： 2017年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,構造,高エネルギーボールミル粉砕により支援された固相反応法により合成した複合ペロブスカイトSr_4(Sr_2Ta_2)O_11の熱的および電気的性質を報告した。熱分析の助けを借りて要求される最終ペロブスカイト相が単段か焼プロセスにより得られた。900°Cで焼成した試料のXRDパターンは,単相二重ペロブスカイト構造の形成を示した。1200°Cで10時間の焼結後の結晶構造は立方晶から可能な酸素空格子点秩序化が原因となった正方晶対称性。焼結したペレットのインピーダンス分光測定を用いて全伝導率の詳細な研究は,580°Cまでの伝導率の増加を示した。しかし,無秩序格子におけるイオン-イオン相互作用,支配し始めるに起因する600°C以上で観察され,全伝導率の低下につながっていた逆効果。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶構造 ,  熱分析 ,  ペレット ,  単相 ,  固相反応 ,  正方晶系 ,  *固相合成 ,  焼結 ,  電気的性質 ,  対称性 ,  X線回折
準シソーラス用語： 伝導率 ,  酸素空格子点 ,  ダブルペロブスカイト ,  ペロブスカイト型構造 , 【Automatic Indexing@JST】

著者キーワード (5件)： ペロブスカイト ,  ボールミリング ,  TEM ,  SEM ,  インピーダンス分光法

分類 (1件)： 酸化物薄膜  (BK14050P)