水熱過程により作製したマンガン酸化物で被覆した階層的コバルト酸化物構造の擬容量性能【Powered by NICT】

Pseudocapacitive performance of manganese oxide coated hierarchical cobalt oxide structure prepared by hydrothermal process

著者 (6件)： Lin C.-K. (School of Dental Technology, College of Oral Medicine, Taipei Medical University, Taipei 110, Taiwan, ROC) ,  Lin P.-C. (Department of Materials Science and Engineering, Feng Chia University, Taichung 407, Taiwan, ROC) ,  Shih S.-J. (Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 106, Taiwan, ROC) ,  Chang C.-J. (Department of Chemical Engineering, Feng Chia University, Taichung 407, Taiwan, ROC) ,  Shi J.-B. (Department of Electronic Engineering, Feng Chia University, Taichung 407, Taiwan, ROC) ,  Chen C.-Y. (Department of Materials Science and Engineering, Feng Chia University, Taichung 407, Taiwan, ROC)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： S1  ページ： S739-S746  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,マンガン(Mn)酸化物堆積した階層的コバルト(Co)酸化物構造は2段水熱プロセスによってスーパーキャパシタ電極として調製した。Co酸化物階層構造は最初の水熱と後熱処理(焼成)プロセスによりグラファイト基板上にテンプレートとして調製した。続いて,Mn酸化物は二次水熱プロセスによってMn酸化物被覆した階層Co酸化物構造を形成するCo酸化物テンプレートの表面上に堆積した。Mn酸化物被覆構造の材料特性と擬容量性能に及ぼすか焼時間の影響を調べた。実験結果は,雪片状形態を有する水熱合成したCo酸化物の微細構造特性を焼成条件によって変化することを示した。Mn酸化物被覆の静電容量の>100%の大きな改善はCo酸化物階層構造を持つテンプレートを用いて得た。さらに,高容量を持つ,Mn酸化物被覆した階層Co酸化物構造の優れたサイクル安定性は,擬似キャパシタとして実用化の高い可能性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *酸化物 ,  水熱合成 ,  グラファイト ,  か焼 ,  微細構造 ,  *マンガン ,  *酸化マンガン ,  形態 ,  階層構造 ,  静電容量 ,  *酸化コバルト ,  後熱処理 ,  コンデンサ
準シソーラス用語： 酸化物被覆 ,  スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (5件)： A粉末:化学的調製 ,  C.電気的性質 ,  E.キャパシタ ,  E.電極 ,  水熱

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： 水 ,  過程 ,  作製 ,  マンガン酸化物 ,  コバルト酸化物