チタン合金の凝固に適用したAl_2O_3に及ぼすY_2O_3ドープBaZrO_3コーティングの作製【Powered by NICT】

Fabrication of Y₂O₃ doped BaZrO₃ coating on Al₂O₃ applied to solidification of titanium alloy

著者 (24件)： Li Chonghe (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Li Chonghe (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Li Chonghe (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Li Mingyang (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Li Mingyang (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Li Mingyang (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Zhang Hao (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Zhang Hao (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Zhang Hao (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Ali Wajid (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Ali Wajid (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Ali Wajid (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Qin Ziwei (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Qin Ziwei (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Qin Ziwei (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Qin Ziwei (Shanghai Special Casting Engineering Technology Research Center, Shanghai 201605, China) ,  Wang Hongbin (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Wang Hongbin (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Wang Hongbin (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Wang Hongbin (Shanghai Special Casting Engineering Technology Research Center, Shanghai 201605, China) ,  Lu Xionggang (State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200072, China) ,  Lu Xionggang (Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai University, Shanghai 200072, China) ,  Lu Xionggang (School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China) ,  Lu Xionggang (Shanghai Special Casting Engineering Technology Research Center, Shanghai 201605, China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 320  ページ： 146-152  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： インベストメント鋳造は,金属成形のための最も多角的な最新技術の一つであるが,セラミックシェル材料の高い化学的安定性はチタン融液の高い活性のために必要である。Al_2O_3は共通の耐火材料,この反応によって引き起こされた融液と汚染との反応のために,チタン合金を鋳造に直接使用できないの一種である。本論文では,新しい鋳造と一方向凝固技術を開発するためにY_2O_3ドープBaZrO_3被覆はAl_2O_3マトリックス上に作製した。マトリックスとしてAl_2O_3を用いて,Y_2O_3ドープBaZrO_3被覆はスラリーをことにより調製,BaZrO_3粉末をdustingとそれらを焼結した。Al_2O_3マトリックスとY_2O_3ドープBaZrO_3被覆の保護被覆,表面品質と化学的安定性の間の反応を,光学顕微鏡(OM),エネルギー分散分光(EDS)および走査電子顕微鏡(SEM)を用いて調べた。その後,Y_2O_3ドープBaZrO_3被覆とチタンメルト間の相互作用を検討した。光学顕微鏡とSEMの結果は,BaZrO_3コーティングは良好な表面形態と高い化学的安定性を有することを示し,EDSの結果は,Al_2O_3マトリックスの間の相互作用層の厚さを示し,保護被覆は焼結時間と温度(1500°Cおよび1600°Cで2 4および6時間)により変化しなかった。拡散層の厚さは,方向性凝固を用いたTi-46Al-8Nbの棒の10μmであった,Ti-6Al-4V合金の鋳造部品の対応した。Y_2O_3ドープBaZrO_3はチタン合金の凝固のための有望な被覆であることを示唆している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 表面性状 ,  *チタン ,  相互作用 ,  光学顕微鏡 ,  *チタン合金 ,  粉体 ,  Ti-6Al-4V合金 ,  *ドーピング ,  焼結 ,  鋳造 ,  走査電子顕微鏡 ,  一方向凝固 ,  *被覆
準シソーラス用語： 融液 ,  化学的安定性 , 【Automatic Indexing@JST】

著者キーワード (4件)： Y_2O_3ドープBaZrO_3コーティング ,  チタン合金 ,  鋳造 ,  方向性凝固

分類 (1件)： 金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (5件)： チタン合金 ,  凝固 ,  ドープ ,  コーティング ,  作製