チタンと二酸化とその特性化研究のルチル相を用いたブルッカイトおよび複合板チタン石の制御された合成【Powered by NICT】

Controlled synthesis of brookite and combined brookite with rutile phases of titanium di-oxide and its characterization studies

著者 (5件)： Balaganapathi T. (Centre for Green Energy Technology, Madanjeet School of Green Energy Technologies, Pondicherry University, Puducherry 605014, India) ,  Kaniamuthan B. (Centre for Green Energy Technology, Madanjeet School of Green Energy Technologies, Pondicherry University, Puducherry 605014, India) ,  Vinoth S. (Centre for Green Energy Technology, Madanjeet School of Green Energy Technologies, Pondicherry University, Puducherry 605014, India) ,  Arun T. (Institute of Physics, Bhubaneswar 751005, India) ,  Thilakan P. (Centre for Green Energy Technology, Madanjeet School of Green Energy Technologies, Pondicherry University, Puducherry 605014, India)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 2  ページ： 2438-2440  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： TiO_2のゾル-ゲル合成のための実験条件を酸触媒の添加と同様にポリエチレングリコール(PEG)を用いて改質した。ルチルとブルッカイトと混合ブルッカイトの合成が得られた。粉末X線回折とマイクロRaman測定はブルッカイトの結晶化を確認した高モル酸濃度とPEG_4000のルチル相を有する低分子酸濃度と混合ブルッカイトの純粋なPEG_4000を用いた。高分解能透過型電子顕微鏡分析は,8と16nmの間のサイズを持つナノ結晶集合体の存在を明らかにした。ルチル相へのブルッカイトからの直接相転移はブルッカイト試料のさらなる熱処理中に観察した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： キレート剤 ,  小分子 ,  複合板 ,  *キャラクタリゼーション ,  *スフェーン ,  *ルチル ,  ナノ結晶 ,  ゾル-ゲル法 ,  ゲル ,  *チタン
準シソーラス用語： HRTEM ,  粉末X線回折 ,  酸触媒 ,  実験条件 ,  *ブルッカイト , 【Automatic Indexing@JST】

著者キーワード (5件)： ゾル-ゲル法 ,  酸触媒 ,  キレート剤 ,  ブルッカイト ,  相転移