リチウムイオンバッテリー用の炭化されたポリドーパミン層によりカプセル化されたシリコン系材料の電気化学的性能を改善するための還元グラフェン酸化物の導入【Powered by NICT】

Introducing reduced graphene oxide to improve the electrochemical performance of silicon-based materials encapsulated by carbonized polydopamine layer for lithium ion batteries

著者 (6件)： Zhou Yu (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Guo Huajun (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Yong Yang (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Wang Zhixing (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Li Xinhai (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Zhou Rong (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China)
資料名： Materials Letters  (Materials Letters)
巻： 195  ページ： 164-167  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： けい素系負極材料の電気化学的性能を改善するために,シリコン/炭化ポリドーパミン/グラフェン(Si/PDAC/rGo)は,グラフェン酸化物を添加したプレコーティングプロセスとその後のアニーリング過程により調製した。ポリドーパミン(PDA)層をもつシリコン粒子はPDA上のアミン基間の相互作用と酸化グラフェン(GO)上の酸素含有基のために,グラフェンシートによってカプセル化した,シリコン粒子の凝集が妨げられた。X線光電子分光法(XPS)の結果は,酸素含有基の大部分は除去され,炭素層は窒素元素を含んでいたことを示した。Si/PDAC/rGoの初期クーロン効率は0.1,0.3,0.5Ag~( 1)で83.8%,84.3%,83.1%であった。Si/PDAC/rGoのサイクルとレート性能は炭化したポリドーパミン層とグラフェンシートの相乗的緩衝効果に起因する増強された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *グラフェン ,  *還元 ,  アミン ,  X線光電子分光法 ,  相互作用 ,  *ケイ素 ,  炭素 ,  酸素 ,  窒素 ,  焼なまし
準シソーラス用語： Coulomb効率 ,  アノード材料【電池】 ,  *酸化グラフェン ,  *電気化学的性能 ,  *ポリドーパミン , 【Automatic Indexing@JST】

著者キーワード (4件)： リチウムイオン電池 ,  シリコン ,  炭素材料 ,  Microstructure

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (6件)： 炭化 ,  ポリドーパミン ,  カプセル ,  シリコン ,  電気化学的性能 ,  還元グラフェン酸化物