高温高圧水中の316ステンレス鋼/インコネル182間の異種溶接部の酸化機構のTEMによる研究【Powered by NICT】

TEM study on oxide mechanism of the dissimilar welds between 316 stainless steels/Inconel 182 in high temperature and high pressure water

著者 (5件)： Wang Wei (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Cao Xinyuan (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Lu Yonghao (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Ding Xianfei (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Shoji Tetsuo (Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579, Japan)
資料名： Materials Characterization  (Materials Characterization)
巻： 131  ページ： 339-347  発行年： 2017年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 高温高圧水における異種溶接部の酸化機構を調べた。結果は溶融境界の両側上の二重構造酸化物層の異なるタイプであることを示した。外部酸化物層では,スピネル酸化物は316SS側に出現したが,インコネル182側上に堆積したフレーク状とスピネル酸化物の成分。内部酸化物膜では,316ステンレス鋼とインコネル182側,スピネル酸化物の形成よりもむしろ316SS側にCr_2O_3,およびこれらのスピネル酸化物の間のいくつかの孔をもたらしたの間に発生したガルバニック腐食,スピネル酸化物とCr_2O_3はインコネル182側上に形成された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 二重構造 ,  フレーク ,  *溶接部 ,  酸化膜 ,  スピネル ,  *ステンレス鋼 ,  電池作用腐食 ,  酸化物
準シソーラス用語： 酸化物層 ,  *高温高圧水 ,  *酸化機構 ,  *Alloy182 ,  *高温高圧 , 【Automatic Indexing@JST】