耐食性,自己洗浄と機械的耐久性の性質を有する鉄基板上のロバストな金超疎水性表面の作製【Powered by NICT】

Fabrication of robust gold superhydrophobic surface on iron substrate with properties of corrosion resistance, self-cleaning and mechanical durability

著者 (5件)： Cui Shuo (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Lu Shixiang (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Xu Wenguo (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  An Baifeng (School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Wu Bei (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 728  ページ： 271-281  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 明確な金ナノフラワー超疎水性表面(SHS)を,化学蒸着とアニールによる鉄箔上に構築した。作製したままの試料は169°までの水接触角(WCA)をもつ優れた超疎水性を発揮し,約3°の滑り角。試料を走査電子顕微鏡(SEM),X線回折パターン(XRD)及びエネルギー分散X線分光分析(EDX)により特性評価形態,構造および組成を決定した。電気化学的測定は,得られた表面は3.5wt%塩化ナトリウム水溶液中で良好な腐食抵抗を示した。SHSに及ぼすpHとpH=2 7および9の試料の腐食抵抗能力の影響を調べた。SHSの自己浄化特性を解析した。,表面は30kPaで2.0mの400グリッドSiC研磨紙による摩耗に耐え,または水がその超疎水性を失い,顕著な機械的耐久性を示すことなく120分間の影響を与える。防食,セルフクリーニング,および機械的耐久性を有する金SHSの成功的製造は多種の実用的状況下のための有望な道を開くことができる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 化学蒸着 ,  *耐久性 ,  X線回折 ,  *鉄 ,  防食 ,  自浄作用 ,  エネルギー分散X線分光分析 ,  *耐食性 ,  *金 ,  塩化ナトリウム ,  走査電子顕微鏡
準シソーラス用語： 滑り角 ,  水接触角 ,  ナノフラワー ,  *超疎水性 , 【Automatic Indexing@JST】

著者キーワード (6件)： 鉄 ,  金 ,  超疎水性 ,  耐食性 ,  自己洗浄 ,  機械的耐久性

分類 (2件)： 腐食  (WB03030B) ,  防食  (WB03040M)