SIC/SIC-AL_2O_3-ムライトナノ複合酸化物被覆を,その場調製法によって調製した。【JST・京大機械翻訳】

Sic/Si-Al_2O_3-mullite Oxidation Protective Coating for C/C Composites Prepared by In-situ Formation Method

著者 (5件)： Tong Ke (C/C Composites Research Center, Key Laboratory of Superhigh Temperature Composites, Northwestern Polytechnical University) ,  Li Hejun (C/C Composites Research Center, Key Laboratory of Superhigh Temperature Composites, Northwestern Polytechnical University) ,  Fu Qiangang (C/C Composites Research Center, Key Laboratory of Superhigh Temperature Composites, Northwestern Polytechnical University) ,  Shi Xiaohong (C/C Composites Research Center, Key Laboratory of Superhigh Temperature Composites, Northwestern Polytechnical University) ,  Li Kezhi (C/C Composites Research Center, Key Laboratory of Superhigh Temperature Composites, Northwestern Polytechnical University)
資料名： Hangkong Xuebao  (Hangkong Xuebao)
巻： 30  号： 3  ページ： 551-556  発行年： 2009年 
JST資料番号： W1470A  ISSN： 1000-6893  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 原料としてSIとAL_2O_3を用いて,SI-AL_2O_3-ムライトナノ(ムライト)被覆を,IN SITU生成法によってSIC被覆炭素/炭素(C/C)複合材料表面上に調製した。SI-AL_2O_3-ムライトナノ被覆の相組成,モルフォロジー,および耐酸化性に及ぼすAL_2O_3含有量の影響を,X線回折,走査型電子顕微鏡,および酸化試験によって研究した。結果は以下を示す。AL_2O_3含有量が30%~40%のとき,コーティングは,主にSI,,およびAL_2O_3相からなり,そして,被覆は,無亀裂であり,そして,酸化防止性能は,最良であった。1500°Cでの等温酸化試験により,SIC/SIC-AL_2O_3-SIC/SIC複合被覆は,SIC被覆のそれよりも,酸化防止性能が著しく改善され,1500°Cでの75時間の等温酸化の後の重量損失は,4.6%であった。コーティング層の主な原因は,コーティング中に不癒合孔隙が生じたことである。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *被覆 ,  重量損失 ,  X線回折 ,  *ムライト ,  亀裂 ,  相組成 ,  被覆層 ,  走査電子顕微鏡 ,  *ナノ複合材料 ,  酸化防止 ,  モルフォロジー ,  *酸化 ,  耐酸化性
準シソーラス用語： 等温酸化 ,  *酸化物被覆 , 【Automatic Indexing@JST】

著者キーワード (5件)： C/C composites ,  coatings ,  oxidation ,  in-situ formation method ,  mullite

分類 (2件)： 金属材料へのセラミック被覆  (YC02050V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (6件)： SiC ,  ムライト ,  ナノ複合 ,  酸化物被覆 ,  調製法 ,  調製