高分子電解質膜燃料電池の部品における酸素輸送抵抗の実験的解析【Powered by NICT】

Experimental dissection of oxygen transport resistance in the components of a polymer electrolyte membrane fuel cell

著者 (5件)： Oh Hwanyeong (Department of Mechanical and Aerospace Engineering, Seoul National University, 1 Gwanak-ro, Gwanak-Gu, Seoul, 08826, Republic of Korea) ,  Lee Yoo il (Department of Mechanical and Aerospace Engineering, Seoul National University, 1 Gwanak-ro, Gwanak-Gu, Seoul, 08826, Republic of Korea) ,  Lee Guesang (Department of Mechanical and Aerospace Engineering, Seoul National University, 1 Gwanak-ro, Gwanak-Gu, Seoul, 08826, Republic of Korea) ,  Min Kyoungdoug (Department of Mechanical and Aerospace Engineering, Seoul National University, 1 Gwanak-ro, Gwanak-Gu, Seoul, 08826, Republic of Korea) ,  Yi Jung S. (JNTG Co.,Ltd., 240-5, Naehyangan-gil, Jeongnam-myeon, Hwaseong-si, Gyeonggi-do, 18523, Republic of Korea)
資料名： Journal of Power Sources  (Journal of Power Sources)
巻： 345  ページ： 67-77  発行年： 2017年 
JST資料番号： B0703B  ISSN： 0378-7753  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 酸素輸送抵抗は,高分子電解質膜燃料電池(PEMFC)の高性能を得るための主要な障害である。酸素輸送を阻害する主要成分を区別するために,PEMFCの成分,基板,ミクロ多孔質層(MPL),触媒層,およびイオノマ膜などの酸素輸送抵抗を分析するため確立した実験的方法。Knudsen数は水銀ポロシメトリまたはBET分析と細孔径を測定することにより,各層で型拡散機構を決定するために計算した。凝縮はほとんど欠けている不飽和条件で,分子拡散抵抗は,不活性ガスのタイプを変えることにより解剖し,イオノマ膜透過は,入口ガス湿度を変化させることによって分離した。さらに,MPLの存在と基板の厚さの変動は,PEMFCの各成分での酸素輸送抵抗を切除することができた。50%以下の低い相対湿度では,イオノマ膜は最大の抵抗を示したが,MPLの寄与は他の加湿条件で最大であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *イオノマ ,  分子拡散 ,  相対湿度 ,  Knudsen数 ,  不活性ガス ,  多孔性 ,  加湿 ,  膜透過 ,  細孔径 ,  湿度
準シソーラス用語： 水銀圧入法 ,  触媒層 ,  *酸素輸送 , 【Automatic Indexing@JST】

著者キーワード (6件)： 酸素輸送抵抗 ,  電流密度の制限 ,  イオノマ ,  ガス拡散層 ,  マイクロ多孔質層 ,  触媒層

分類 (1件)： 燃料電池  (YB04040V)

タイトルに関連する用語 (3件)： 高分子電解質膜燃料電池 ,  酸素輸送 ,  実験的解析