整形外科応用のためのナノ結晶ダイヤモンド被覆Ti基合金の摩擦腐食と電気化学的挙動【Powered by NICT】

Tribocorrosion and electrochemical behaviour of nanocrystalline diamond coated Ti based alloys for orthopaedic application

著者 (6件)： Gopal Vasanth (Department of Physics, School of Advanced Sciences, VIT University, Vellore 632014, India) ,  Chandran Maneesh (Materials Science Research Centre, Department of Physics, IIT Madras, Chennai, India) ,  Rao M.S. Ramachandra (Materials Science Research Centre, Department of Physics, IIT Madras, Chennai, India) ,  Mischler Stefano (Tribology and Interface Chemistry Group, Ecole Polytechnique Federale de Lausanne (EPFL), Switzerland) ,  Cao Shoufan (Tribology and Interface Chemistry Group, Ecole Polytechnique Federale de Lausanne (EPFL), Switzerland) ,  Manivasagam Geetha (Centre for BioMaterials Science and Technology, School of Mechanical & Building Sciences, VIT University, Vellore 632014, India)
資料名： Tribology International  (Tribology International)
巻： 106  ページ： 88-100  発行年： 2017年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 股関節および膝関節のような金属インプラントは,しばしば摩耗と腐食の組合せ作用のために失敗する。金属インプラント上のナノ結晶ダイヤモンド(NCD)被覆は,この問題を克服するための有力な候補となり得る。本研究では,熱フィラメント化学蒸着(HFCVD)法を用いたCp-Ti,Ti-6Al-4VおよびTi-13Nb-13Zr上に堆積したナノ結晶ダイヤモンド(NCD)コーティングのトライボ腐食と電気化学的挙動を調べた。結果は結晶間細孔,TiC中間層,および電気伝導率のような因子は,すべてのNCDコーティングの電気化学的挙動に影響することを示した。トライボ腐食下で,開路電位(OCP)における説明できないシフトは,滑りの開始で注目された。さらに,滑り過程で観察されたOCPの連続的低下。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *被覆 ,  *ナノ結晶 ,  細孔 ,  *電気化学的挙動 ,  *チタン合金 ,  股関節 ,  *チタン ,  電気伝導率 ,  膝関節 ,  *結晶 ,  *腐食 ,  開路
準シソーラス用語： 中間層 ,  HFCVD ,  *ダイヤモンド被覆 , 【Automatic Indexing@JST】

著者キーワード (4件)： ナノ結晶ダイヤモンドコーティング ,  チタン合金 ,  腐食 ,  トライボ腐食

分類 (2件)： 潤滑一般  (QB02010S) ,  腐食基礎理論,腐食試験  (WB03020Q)

タイトルに関連する用語 (7件)： 整形外科 ,  応用 ,  ナノ結晶ダイヤモンド ,  Ti基合金 ,  摩擦 ,  腐食 ,  電気化学的挙動