全グラフェンベースリチウムイオンキャパシタのアノードとしての窒素ドープ欠陥グラフェンエアロゲル【Powered by NICT】

Nitrogen-Doped Defective Graphene Aerogel as Anode for all Graphene-Based Lithium Ion Capacitor

著者 (25件)： Wang Xin (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Xin (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Xin (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Zhenkun (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Zhenkun (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Zhenkun (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Xin (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Xin (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Xin (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Peng Huifen (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Peng Huifen (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Peng Huifen (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Xin Guoqing (Department of Mechanical, Aerospace, and Nuclear Engineering, Rensselaer Polytechnic Institute, Troy, New York, 12180-3590, USA) ,  Lu Chengxing (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Lu Chengxing (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Lu Chengxing (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Zhong Yuxiang (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Zhong Yuxiang (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Zhong Yuxiang (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Gongkai (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Gongkai (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Wang Gongkai (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Yongguang (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Yongguang (School of Material Science & Engineering, Hebei University of Technology, Tianjin, 300130, China) ,  Zhang Yongguang (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, Hebei University of Technology, Tianjin, 300130, China)
資料名： Chemistryselect  (Chemistryselect)
巻： 2  号： 27  ページ： 8436-8445  発行年： 2017年 
JST資料番号： W2528A  ISSN： 2365-6549  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 窒素ドープ欠陥グラフェンエアロゲル(N DGA)は温和な細孔形成とポストドーピングプロセスを組み込んだ水熱法により調製した。微細構造と電気化学的挙動を評価した。比較的高レベル窒素含有量のNDGAは三次元(3D)相互接続した構造であり,しわ状のグラフェンは明白な面内細孔を提示したを維持する。1387と143mAh/g~( 1)の比容量は五万千mA g~( 1)の電流密度で達成することができた。構造変更無しでグラフェンエアロゲル(GA)のそれとは対照的にアノードとして大きく改善された電気化学的性能は,3D微細構造,ヘテロ原子ドーピングと欠陥サイトに帰することができる。これらの特徴は,高度に利用可能な表面積,改善された伝導度,効率的なイオン輸送と電気化学的活性表面,可逆的リチウムイオン貯蔵,定格,ならびに安定性に有利であることが全電極を与える。NDGAアノードと欠陥のあるグラフェンエアロゲル/活性炭(DGA/AC)カソードを用いてLIC完全セルが組み立てられ,対応する性能も評価した。39Wh kg~( 1)と1.2kW kg~( 1)の最大エネルギー密度と電力密度を供給することができた。降下性能が高エネルギー/パワー密度を有する全てのグラフェンベースLICの有望な展望を示した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 水熱合成 ,  活性炭 ,  イオン輸送 ,  微細構造 ,  エネルギー密度 ,  電気化学 ,  電流密度 ,  電気化学的挙動 ,  *グラフェン ,  細孔
準シソーラス用語： 電力密度 ,  *リチウムイオン ,  電気化学的性能 ,  比容量 ,  *窒素ドーピング , 【Automatic Indexing@JST】

著者キーワード (5件)： アノード ,  欠陥 ,  グラフェンエアロゲル ,  リチウムイオンキャパシタ ,  窒素ドーピング

分類 (2件)： 二次電池  (YB04030K) ,  炭素とその化合物  (YB02060D)

タイトルに関連する用語 (3件)： アノード ,  窒素ドープ ,  欠陥