標準座標及び非標準プライ方向を持つ積層板の衝撃後圧縮強度の実験的研究【Powered by NICT】

Experimental study into compression after impact strength of laminates with conventional and nonconventional ply orientations

著者 (6件)： Liv Yi (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain) ,  Guillamet G. (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain) ,  Costa J. (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain) ,  Gonzalez E.V. (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain) ,  Marin L. (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain) ,  Mayugo J.A. (AMADE, Polytechnic School, University of Girona, Campus Montilivi s/n, 17003, Girona, Spain)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 126  ページ： 133-142  発行年： 2017年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 調整積層順序による衝撃損傷許容性積層材料の探求は,層配列は0±45°Cと90°Cに限定されない非従来型積層材をもたらした。衝撃後圧縮(CAI)強さである剥離の存在によって損なわれることを仮説から出発して,小さな剥離を持つ中央積層体を維持しないようにプライ間のミスマッチ角を選択することにより定義された層配列。実験キャンペーンは,この仮説を検証した。その目的のために,ベースラインとブロックされたプライ積層材を研究に含めた。試料を低速度衝撃に続くASTM規格に従って,圧縮下で試験した。層間剥離は,超音波Cスキャンで同定した。結果は不整合角を制御することにより所定の成功している剥離位置だけでなく,衝撃後の圧縮強度保持におけるその後の改善を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査 ,  ASTM規格 ,  *圧縮強さ ,  不整合 ,  *積層板 ,  層間剥離 ,  *衝撃 ,  基準線 ,  超音波 ,  積層材料 ,  低速度
準シソーラス用語： 損傷許容性 ,  積層順序 ,  *実験研究 ,  *衝撃後圧縮強さ , 【Automatic Indexing@JST】