境界潤滑鋼-鋼接触における軸受鋼の摩耗とマイクロピッチング挙動に及ぼす超音波ナノ結晶表面改質の影響【Powered by NICT】

Effects of ultrasonic nanocrystal surface modification on the wear and micropitting behavior of bearing steel in boundary lubricated steel-steel contacts

著者 (7件)： Qin Haifeng (The Timken Engineered Surfaces Laboratories, The University of Akron, Akron, OH, USA) ,  Qin Haifeng (Department of Chemical Engineering, The University of Akron, Akron, OH, USA) ,  Ren Zhencheng (Department of Mechanical Engineering, The University of Akron, Akron, OH, USA) ,  Zhao Jingyi (Department of Mechanical Engineering, The University of Akron, Akron, OH, USA) ,  Ye Chang (Department of Mechanical Engineering, The University of Akron, Akron, OH, USA) ,  Doll G.L. (The Timken Engineered Surfaces Laboratories, The University of Akron, Akron, OH, USA) ,  Dong Yalin (Department of Mechanical Engineering, The University of Akron, Akron, OH, USA)
資料名： Wear  (Wear)
巻： 392-393  ページ： 29-38  発行年： 2017年 
JST資料番号： E0377A  ISSN： 0043-1648  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 超音波ナノ結晶表面改質(UNSM)技術を用いて,AISI-52100鋼試験片とスラスト玉軸受レースウェイを治療に用いられている。未処理試料のトライボロジー性能について,境界潤滑状態下での往復滑りと転がり/滑り接触におけるUNSM処理した試験片と比較した。試料の表面プロフィルと表面粗さの摩擦と摩耗係数,微小孔食,と変化を調べた。結果は,UNSM処理試料は未処理試料よりも,より高い摩耗と微小孔食抵抗を持つことを示した。摩耗と微小孔食抵抗性の改善は,UNSM処理の結果として表面領域近傍の増加した表面硬度,微細化した結晶粒サイズと圧縮残留応力に起因すると考えられる。UNSM技術は,軸受,ギヤおよびシールのような機械部品の接触面の耐久性およびトライボロジー性能を改善するための強力なツールであることが証明されている。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 耐孔食性 ,  *表面改質 ,  *軸受鋼 ,  *ナノ結晶 ,  結晶粒径 ,  トライボロジー ,  滑り接触 ,  *摩耗 ,  *境界潤滑 ,  *軸受 ,  *鋼 ,  玉軸受 ,  耐久性 ,  *超音波
準シソーラス用語： 接触面 , 【Automatic Indexing@JST】

著者キーワード (4件)： UNSM ,  ころがり-すべり ,  摩耗 ,  マイクロピッチング

分類 (2件)： 潤滑一般  (QB02010S) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (8件)： 境界潤滑 ,  鋼 ,  軸受鋼 ,  摩耗 ,  挙動 ,  超音波 ,  ナノ結晶 ,  表面改質