アルミニウム合金AA5083の鋭敏化の程度に及ぼす復元処理の効果【Powered by NICT】

The effect of reversion heat treatment on the degree of sensitisation for aluminium alloy AA5083

著者 (8件)： Zhang R. (Materials Genome Institute, Shanghai University, Shanghai, 200072, China) ,  Zhang R. (Department of Materials Science and Engineering, Monash University, Clayton, VIC, 3800, Australia) ,  Zhang Y. (Department of Materials Science and Engineering, Monash University, Clayton, VIC, 3800, Australia) ,  Zhang Y. (National Engineering Research Centre of Light Alloy Net Forming and State Key Laboratory of Metal Matrix Composite, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Yan Y. (Department of Materials Science and Engineering, Monash University, Clayton, VIC, 3800, Australia) ,  Thomas S. (Department of Materials Science and Engineering, Monash University, Clayton, VIC, 3800, Australia) ,  Davies C.H.J. (Department of Mechanical and Aerospace Engineering, Monash University, Clayton, VIC, 3800, Australia) ,  Birbilis N. (Department of Materials Science and Engineering, Monash University, Clayton, VIC, 3800, Australia)
資料名： Corrosion Science  (Corrosion Science)
巻： 126  ページ： 324-333  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 自然増感場検索されたAA5083(Al Mg Mn)試料に及ぼす復元処理の詳細な研究を行った。研究復帰温度は150と240°C,β相(Mg_2Al_3)変態温度を張るの間であった。前と復帰後感作(DoS)の程度は,硝酸質量損失試験(NAMLT)で調べた;逆戻り熱処理の影響を明らかにする主に逆変態温度の影響を受けた。逆変態処理試料のDoSは粒界β相連続性に相関していたが,ここで定量的電子顕微鏡によって評価された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 増感 ,  電子顕微鏡 ,  逆変態 ,  β相 ,  *合金 ,  硝酸 ,  *アルミニウム合金 ,  結晶粒界 ,  転移温度 ,  粒界腐食 ,  連続性 ,  感作 ,  熱処理
準シソーラス用語： 質量損失 ,  *AA5083 , 【Automatic Indexing@JST】

著者キーワード (5件)： Aアルミニウム ,  A合金 ,  B SEM ,  B STEM ,  C.粒界腐食

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (4件)： アルミニウム合金 ,  AA5083 ,  程度 ,  復元